Polymer Property : Flexural Modulus = 1160 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	8.00 GPa	1160 ksi	ISO 178
Polyplastic Armamid® PA GF25-1FR Nylon 6, 25% Glass Fiber Flame retardant, RoHS compliantInformation provided by PolyPlastic Group.
Flexural Modulus	8.00 GPa @Temperature 23.0 °C	1160 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB POLYfill PPH GF8030 HC Polypropylene Homopolymer, Glass Fibre-Reinforced Information provided by Polykemi AB
Flexural Modulus	8.00 GPa	1160 ksi	ISO 178
Hexion Bakelite™ PF 2535 Phenolic Formaldehyde Resin, High Surface Quality, Dishwasher Proof (discontinued ** Phenolic molding compound, inorganically/organically filled, average heat resistant, steam resistant, dish washer proof, high surface quality.Application areas: Fittings for ovens and dishwashers, t..
Flexural Modulus	8.00 GPa	1160 ksi	ISO 178
Hexion Bakelite™ 151733 Phenolic Formaldehyde Resin (discontinued **) Phenolic molding compound, mainly organically filled, standard molding compound for normal stress.Application areas: Contact strips.Information provided by Bak AGBak AG became a part of Hexion in 20..
Flexural Modulus	8.00 GPa	1160 ksi	ISO 178
Hexion Bakelite™ X65 Phenolic Formaldehyde Resin, UL Listed (discontinued **) Phenolic molding compound, inorganically/organically filled, good heat-resistance and dimensional stability, UL listed molding compound 3.0 mm/V-0 (BN, BK).Application areas: Oven strips.Information..
Flexural Modulus	8.00 GPa	1160 ksi
Lehmann & Voss LUVOCOMÂ® 20-8332 Polyphthalamide, with glass fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Low influence from moisture and temperature to measures and electrical prop..
Flexural Modulus	8.00 GPa	1160 ksi
Lehmann & Voss LUVOCOMÂ® 80-7555/BK Polyacetal-copolymer, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; low thermal coefficient of expansion.Electrically conductive, suitable for..
Flexural Modulus	8.00 GPa @Temperature 22.0 Â°C	1160 ksi @Temperature 71.6 Â°F	25 mm wide 100 mm long, flat samples; ISO 14125
Menzolit MenzolitÂ® SMC 1650 Unsaturated Polyester UP SMC 1650 is a specially designed anti-microbial polyester moulding compound which incorporates a "germ killer" . It has been tested and found to be compliant for resistance to fungal defacement in ..
Flexural Modulus	8.00 GPa	1160 ksi
Lehmann & Voss LUVOCOMÂ® 1100-8326 Polyether sulfone, with carbon fiber, PTFE, lubricant modified Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.Strong, stiff parts.Dy..
Flexural Modulus	8.00 GPa	1160 ksi	ASTM D790
Techmer ES HiFillÂ® PA6 GF/M40 HS L 40% Glass/Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral, 40% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedTPCI# 7395102Informat..
Flexural Modulus	8.00 GPa	1160 ksi	ASTM D790
Techmer ES HiFillÂ® PA6 GF/M40 IG BK 40% Glass/Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral, 40% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedProcessing Method: In..
Flexural Modulus	8.00 GPa	1160 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp CF006 PS (Europe-Africa-Middle East) LNP* Thermocomp* CF006 is a compound based on Polystyrene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Modulus	8.00 GPa	1160 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp RF0057E PA 66 (Europe-Africa-Middle East) LNP* Thermocomp* RF0057E is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Non-Brominated & Non-Chlorinated Flame Retardant.Thi..
Flexural Modulus	8.01 GPa	1160 ksi	ASTM D 790
SABIC Innovative Plastics LNP Thermocomp RF006Q PA 66 (Asia Pacific) LNP* Thermocomp* RF006Q is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Reduced Moisture.This data was supplied by SABIC-IP for the Asia Pacif..
Flexural Modulus	7.97 GPa	1160 ksi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP PF006S PA 6 LNP THERMOCOMP* PF006S is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized.
Flexural Modulus	8.00 GPa	1160 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GFN3 PPE+PS PPE+PS blend. 30% Glass reinforced. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Sui..
Flexural Modulus	8.00 GPa	1160 ksi	ASTM-D790
Polyram PlusTek PA301G6 Nylon 6.6, Heat Stabilized, 30% Glass Fiber Heat stabilized, 30% glass fiber reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Modulus	8.00 GPa	1160 ksi	ASTM-D790
Polyram PlusTek PA303G5 Nylon 6.6, 25% Glass Fiber 25% glass fiber reinforced, heat stabilized and hydrolysis resistant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Modulus	8.00 GPa	1160 ksi	ASTM-D790
Polyram PlusTek PB300G5 Nylon 6, 15% Glass Fiber 15% glass-fiber reinforced, heat stabilized polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Modulus	8.00 GPa	1160 ksi	ASTM-D790
Polyram PlusTek PB304G7 Nylon 6, 35% Glass Fiber 35% glass-fiber reinforced, heat stabilized and impact modified polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Modulus	8.00 GPa	1160 ksi	ASTM-D790
Polyram RamShine PV300G6 ABS, 30% Glass Fiber 30% glass fiber reinforced, heat resistance and minimal mold shrinkage ABS for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Modulus	8.00 GPa	1160 ksi	ISO 178
Polyram RamSter PF306G6 PBT, 30% Glass Fiber 30% Glass fiber reinforced, low viscosity PBT for injection molding applications.Information provided by Polyram.
Flexural Modulus	8.00 GPa	1160 ksi	ISO 178
Eurostar Starflam PF0057E PA6, 25% Glass Filled, Injection Molded Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Fiber Reinforced, Polyamide 6 Injection Molding Resin (also known as PF-1005 Z270)Information provided by Polymer Technology & Services,..
Flexural Modulus	8.00 GPa	1160 ksi	ISO 178
BASF Ultramid® A3EG7 35% Glass Filled PA66 (Conditioned) Ultramid A3EG6 is a 35% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability.
Flexural Modulus	8.00 GPa	1160 ksi	ASTM D790
Beijing Chemical Industry KAIFA® 201-G30 PBT Resin 30% glass fiber reinforcedInformation provided by Beijing Chemical Industry Research Institute (Group)
Flexural Modulus	8.00 GPa	1160 ksi	ASTM D790
Beijing Chemical Industry KAIFA® 301-G30 PBT Resin 30% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group)
Flexural Modulus	8.00 GPa	1160 ksi	ASTM D790
Beijing Ranger Chem PBT-201-G30 272 Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin..
Flexural Modulus	8.00 GPa	1160 ksi	ASTM D790
BLUESTAR 201-G30202 PBT, 30% Glass Filled Typical Applications: Energy saving lighting, E/E applicationsInformation provided by Polymer Technology and Services, LLC (PTS).
Flexural Modulus	8.00 GPa @Temperature 120 °C	1160 ksi @Temperature 248 °F	ASTM D790
LATI LARTON G/40 40% Glass Fiber Filled Polyphenylene sulfide (PPS) (Unverified Data**) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex..