A. Schulman POLYFLAM™ RPP 1058 General Purpose Homopolymer Polypropylene (30% Fiberglass)

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	A. Schulman POLYFLAM™ RPP 1058 General Purpose Homopolymer Polypropylene (30% Fiberglass).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

DescriptionPolyflam® RPP 1058 is a general purpose homopolymer polypropylene flame retardant with a UL-V2 flammability rating and 105°C temperature index at 0.030 in.Information provided by A. Schulman.

Physical Properties	Metric	English	Comments
Specific Gravity	0.950 g/cc	0.950 g/cc	ASTM D792
Linear Mold Shrinkage	0.015 - 0.020 cm/cm	0.015 - 0.020 in/in	ASTM D955
Melt Flow	12 g/10 min	12 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
Elongation at Break	200 %	200 %	ASTM D638
Flexural Modulus	1.20 GPa	174 ksi	ASTM D790
Izod Impact, Notched	0.300 J/cm	0.562 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	55.0 °C	131 °F	ASTM D648
UL RTI, Electrical	105 °C	221 °F	0.030 in; UL 94
Flammability, UL94	V-2 @Thickness 0.780 mm	V-2 @Thickness 0.0307 in
	V-2 @Thickness 1.57 mm	V-2 @Thickness 0.0618 in
	V-2 @Thickness 3.05 mm	V-2 @Thickness 0.120 in