Aclo Accucomp ABS ABS892BL High Heat Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Aclo Compounders |
| Trade Name | Accucomp |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accucomp ABS ABS892BL High Heat Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | MD; ASTM D955 |
| Melt Flow | 0.80 g/10 min | 0.80 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 104 | 104 | ASTM D785 |
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 1.700 GPa | 246.5 ksi | ASTM D638 |
| Flexural Strength | 71.98 MPa | 10440 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Izod Impact, Notched | 3.68 J/cm | 6.90 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 97.8 °C | 208 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL File #E56070 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering E50E Ethylene Propylene Rubber
- Ineos Nova 2580 General Purpose Crystal Polystyrene (discontinued **)
- Kennametal Stellite Nistelle 625 Nickel Superalloy
- Borealis FR4810 Low Smoke Zero Halogen Flame Retardant Jacketing Compound
- A. Schulman POLYBATCH™ Grey 8368 Concentrate Based In Polyethylene
- Dymax 3-20556 Solvent-Free Plastic Adhesive
- Asahi Glass Fluon® RB1211 15% Glass Fiber, 5% MoS2, PTFE Filled Compound
- A. Schulman POLYFORT™ FPP 2496 Injection Molding Grade, Mineral Fortified Polypropylene
Copyright © lookpolymers.com All Rights Reserved