- Aremco Ceramacast™ 510 High Temperature Potting & Casting Material Alumina
Aremco Ceramacast™ 510 High Temperature Potting & Casting Material Alumina
| Category | Ceramic , Oxide , Aluminum Oxide , Potting/Casting Ceramic |
| Manufacturer | Aremco |
| Trade Name | Ceramacast™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Ceramacast™ 510 High Temperature Potting & Casting Material Alumina.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Coarse grain castable for producing large hi-temp tooling.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 1.79 g/cc | 0.0648 lb/in³ | Powder |
| Porosity | <= 7.00 % | <= 7.00 % | |
| pH | 3.0 - 4.0 | 3.0 - 4.0 | |
| Viscosity | 12000 cP | 12000 cP | mixed |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Compressive Strength | 55.2 MPa | 8000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 7.02 µm/m-°C @Temperature 20.0 °C |
3.90 µin/in-°F @Temperature 68.0 °F |
|
| Maximum Service Temperature, Air | 1760 °C | 3200 °F | |
| Shrinkage | <= 1.00 % @Temperature 538 °C |
<= 1.00 % @Temperature 1000 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | |
| Dielectric Strength | 2.95 kV/mm | 75.0 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 1800 min | 30.0 hour | Cover mold with polyethylene sheet or locate in a humidity chamber for 24 hrs; 3 hrs at 200°F; 3 hrs at 250°F |
| Pot Life | 120 - 180 min | 120 - 180 min | |
| Shelf Life | 12.0 Month | 12.0 Month |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Acid Resistance | Good | attacked by HF |
| Alkali Resistance | Good | |
| Color | Light Gray | |
| Mix Ratio | 100:15-19 | powder:liquid |
| Moisture Resistance | Good |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA-1000 IG Clear High Impact Acrylic Resin
- Proto3000 Objet Digital Materials™ DM_9110/9410/9210/9310 Rubber-like Prototyping Polymer
- Lehmann & Voss LUVOCOM® 1850-7315 PBT, with carbon fiber
- Mitsui Arlenâ„¢ C230 30% Glass Fiber-Reinforced Modified Nylon 6T (DAM)
- Materion Beryllium Copper Alloy M25 Rod and Bar; H (TD04) Temper; over 9.5 to 25.4 mm (UNS C17300)
- Multibase C6-265 DI-CUP R Dow-Corning Class VI Elastomer
- Fainplast Compounds FKT 92 Flexible PVC, Insulation Lead Free
- Asahi Kasei Tenac®-C CF452 Copolymer Polyacetal Resin
- Addcomp PRIEX® Ionomer 40101 PP homopolymer
- ExxonMobil Fenso 71
Copyright © lookpolymers.com All Rights Reserved