Arkema Group Orgalloy® R 60T30 Nylon 6 Alloy, Mineral Filled (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled
Manufacturer	Arkema
Trade Name	Orgalloy®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Orgalloy® R 60T30 Nylon 6 Alloy, Mineral Filled (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Rigid polyamide 6 alloy: easy to process, low moisture absorption, chemical resistance (no known solvents).Mineral filled. Low distortion, offers precisely dimensioned injection moldings.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.27 g/cc	0.0459 lb/in³
Water Absorption	2.5 %	2.5 %
Moisture Absorption at Equilibrium	1.0 %	1.0 %	Humidity Absorption
Melt Flow	6.0 g/10 min @Load 2.16 kg, Temperature 235 °C	6.0 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	52.0 MPa	7540 psi	5 mm/min
Elongation at Break	2.6 %	2.6 %	5 mm/min
Tensile Modulus	4.80 GPa	696 ksi	1 mm/min

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10°C/min
Deflection Temperature at 0.46 MPa (66 psi)	190 °C	374 °F
Deflection Temperature at 1.8 MPa (264 psi)	110 °C	230 °F
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in
Oxygen Index	22 %	22 %

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	600 V	600 V