Chesterton 633 SXCM Synthetic, Extreme Pressure & Corrosion Resistant Grease-with Moly

Category Fluid , Lubricant
Manufacturer Chesterton
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chesterton 633 SXCM Synthetic, Extreme Pressure & Corrosion Resistant Grease-with Moly.pdf
  Online Service   lookpolymers   27660005
Material Notes:
Description: Chesterton® 633 Synthetic Extreme Pressure & Corrosion Resistant Grease with Moly is the one grease to use for the most demanding lubricating needs. It is a multi-purpose workhorse with outstanding extreme pressure and anti-wear capabilities, shear stability, temperature and corrosion resistance. As a premium quality, water resistant grease, 633 will not be removed even in severe water washout situations. Chesterton 633 can be used in steam and direct water contact services. With a dropping point of 288°C (550°F). It will not melt and run out even at high speeds or under heavy loads as found in Mining, Metal Processing, Steel, Aluminum or Copper Manufacturing Industry. 633 SXCM is greatin its ability to extend bearing life, reduce equipment repairs and improve operational efficiency of grease lubricated equipment. It is especially advantageous where there is exposure to high humidity, corrosive vapors and shock loading or vibration as found in pulp and paper mills, mining operations, power generating plants, steel mills and metal forming operations. Applications include the lubrication of pinch roll and press roll bearings, dryer and calendar roll bearings, corrugators and sitters, blowers and fan bearings, oven conveyors bearings, cranes and mechanical presses. Features:Virtually impervious to water and steamSynthetic Base FluidCompatible with most elastomers and sealsSmooth Tack TextureAdheres to MetalOutstanding Extreme Pressure ResistanceWater and Corrosion ResistantWide temperature range.Suggested Uses: Use in all applications where conventional grease break down under shear, thermal abuse, shock loading and water contamination. Chesterton 633 SXCM can be used whenever thermally stable grease is required.Applications:Slides, guides, plain bearings and bushings.Anti-friction bearings, roller bearings and ball bearingsKiln Ring, Shoe and RollersCouplings, joints and splined shaftsMining Equipment,Off RoadCranes, Drag LinesRailways, Switch Gear and Curve LubricationLubricating Additives: Non Heavy Metal, Extreme Pressure and Anti-Wear, Anti-Fretting Additives, Surface Reactive Anti-Rust and Corrosion Additives, Oxidation InhibitorsInformation provided by Chesterton
Physical Properties Metric English Comments
Specific Gravity 0.950 - 1.05 g/cc
0.950 - 1.05 g/cc
Viscosity Measurement 141
Base Oil; ASTM D445
Kinematic Viscosity at 40°C (104°F) 35 cSt
35 cSt
Base Oil; ASTM D445
Kinematic Viscosity at 100°C (212°F) 6.5 cSt
6.5 cSt
Base Oil; ASTM D445
Mechanical Properties Metric English Comments
Four Ball Extreme Pressure, Load Wear Index 140
ASTM D2596, DIN 51 350/4
Four Ball Extreme Pressure, Weld Load 800 kg
1760 lb (mass)
ASTM D2596, DIN 51 350/4
Four Ball Wear 0.380 mm

@Temperature 75.0 °C,
Time 3600 sec
0.0150 in

@Temperature 167 °F,
Time 1.00 hour
1200 rpm, 40 kg, scar diameter; ASTM D2266, DIN 51 350/5
Penetration 310 - 340
310 - 340
ASTM D217, DIN ISO 2137
Timken Test 29500 g
65.0 lb
ASTM D2509
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 250 °C
482 °F
Minimum Service Temperature, Air -50.0 °C
-58.0 °F
Dropping Point 288 °C
550 °F
ASTM D2265, DIN 51 801/1
Descriptive Properties Value Comments
Bearing Life 200 hrs
ASTM D3527
Bomb Oxidation 3 psi drop
1000 hrs, ASTM D942
Color Bright, Silver
Consistency 1
NLGI, DIN 51 818
Copper Corrosion 0/1B
ASTM D4048, DIN 51 811
Corrosion Resistance >1000 hrs
@ 50 microns film thickness, 5% NaCl, ASTM B117
Oil Base PAO Synthetic
Texture Smooth, Tacky
Thickener Proprietary, Patent Protected, Sulfonate Complex
Water Washout Resistance <2.0%
@79°C, ASTM D1264
Worked Stability -0.01
10000 Strokes, ASTM D217
10000 Strokes, ASTM D217