- Chi Mei Polyrex® PH-88 Polystyrene - High Impact
Chi Mei Polyrex® PH-88 Polystyrene - High Impact
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polyrex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polyrex® PH-88 Polystyrene - High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High impact
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Melt Flow | 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 84.0 MPa | 12200 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 22.0 MPa | 3190 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 56 % | 56 % | 50 mm/min; ISO 527 |
| Flexural Strength | 35.0 MPa | 5080 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.20 GPa | 174 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 179 |
| Impact | 12.0 | 12.0 | Impact Flexural Test Notched (KJ/m²) |
| 100 | 100 | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | unannealed; ISO 75 |
| 89.0 °C | 192 °F | annealed; ISO 75 | |
| Vicat Softening Point | 87.0 °C @Load 5.00 kg |
189 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 89.0 °C @Load 5.00 kg |
192 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 96.0 °C @Load 1.00 kg |
205 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 98.0 °C @Load 1.00 kg |
208 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- Oxford Polymers PEI 1010 PEI
- Silikony Polskie Polimer MV 0.07 Methylvinylsilicone Gum
- Teknor Apex APEX® 3210-55 Polyvinyl Chloride, Flexible
- Saint-Gobain Tygon® F-4040-A Fuel and Lubricant Tubing Formulation
- Goodfellow Ni-Mn-Ga Magnetic Shape Memory Alloy (MSM)
- Zeon Chemicals Zetpol® 4310 Hydrogenated Nitrile Elastomomer
- DSM Arnite® TV4 261 PBT-30% Glass Reinforced (European and Asian Grade)
- Arkema Group Rilsan® BMV Nylon 11 (Dry)
- Bulk Molding Compounds BMC 102 Glass Filled Thermoset Polyester
- Indium Corp. Indalloy 203 Indium Solder Alloy
Copyright © lookpolymers.com All Rights Reserved