Eurostar Staramide 6 80E10 PA6, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide 6 80E10 PA6, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide 6 80E10 is a high density, Polyamide 6, Injection Molding Resin (also known as 680E10)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.00 g/cc | 0.145 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.011 - 0.013 cm/cm @Thickness 4.00 mm |
0.011 - 0.013 in/in @Thickness 0.157 in |
E2P method |
| Ash | 82 % @Temperature 650 °C |
82 % @Temperature 1200 °F |
ISO 3451 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.40 GPa | 783 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 250 - 260 °C | 482 - 500 °F | |
| Zone 2 | 260 - 280 °C | 500 - 536 °F | |
| Zone 3 | 260 - 280 °C | 500 - 536 °F | |
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Pyrotek Pyroslip 105 RFU High-Purity Graphite-Based Lubricant
- SABIC Innovative Plastics Lexan® 4501 PC (Europe-Africa-Middle East)
- Polymer Resources PC-GP3-TFE5 Polycarbonate, 5% PTFE, High Flow, Wear Resistant
- Hybrid Plastics PO6C81.01 Nanoreinforced® Polyphenylene Oxide (PPO)
- A. Schulman POLYFORT™ FPP 1236-2939 Fiberglass Reinforced Homopolymer Polypropylene
- A. Schulman POLYFORT™ FPP 1609 Mica Fortified Copolymer Polypropylene
- Trelleborg Emerson & Cuming Eccobond® 286 Two-Component General Purpose Epoxy Adhesive
- Arkema Group Lacovyl® GB 9010 M PVC
Copyright © lookpolymers.com All Rights Reserved