Fibre Glast EZ Poxy EZ10 / EZ83 Epoxy (discontinued **)
| Category | Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fibre Glast EZ Poxy EZ10 / EZ83 Epoxy
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Fibre Glast Developments Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | |
| Viscosity | 750 cP | 750 cP | ASTM D2293 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 88 | 88 | Cured; ASTM D2240 |
| Tensile Strength at Break | 281.8 MPa | 40870 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 |
| Elongation at Break | 1.97 % | 1.97 % | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 |
| Tensile Modulus | 14.7 GPa | 2130 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content. |
| Flexural Strength | 308.98 MPa | 44814 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 |
| Flexural Modulus | 19.5 GPa | 2830 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | 64.4 °C | 148 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Pot Life | 120 min @Temperature 25.0 °C |
120 min @Temperature 77.0 °F |
4 fl. Oz.; ASTM D2471 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Mix Ratio | 100:44 | Resin:Hardener by Weight |
| 2.13:1 | Resin:Hardener by Volume |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S70X Silicone Rubber
- Precision Polymer Engineering V60F Fluoroelastomer Compound
- Premix Thermoplastics PREWHITE PE 10-50
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Carbon Black, N-220 (ISAF)
- Taiwan Sheen Soon Sheenthane® A9070A Film Grade Thermoplastic Polyurethane Elastomer
- Solvay Specialty Polymers Amodel® AT-1001L Polyphthalamide (PPA)
- Ecomass® 1080ZD95 Tungsten Filled Polyamide
- Eurostar Starflam P10002Z PA6, Flame Retardant, Extrusion
- Braskem EB861/51 Blown Film Extrusion Low Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved