Haynes Waspaloyâ„¢ alloy, sheet

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes Waspaloyâ„¢ alloy, sheet.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Age-hardenable superalloy with very good strength at temperatures up 980°C (1800°F), can be cold-formed in the annealed condition, may also be hot formed at 1040°C (1900°F) and above, good resistance to gas turbine combustion gas environments at temperatures up to 870°C (1600°F). Widely used as a wrought material for forged and fabricated gas turbine and aerospace components.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.20 g/cc
0.296 lb/in³
at RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1335 MPa
193600 psi
83.0 MPa

@Temperature 1095 °C
 12000 psi

@Temperature 2003 °F
220 MPa

@Temperature 980 °C
 31900 psi

@Temperature 1800 °F
545 MPa

@Temperature 870 °C
 79000 psi

@Temperature 1600 °F
970 MPa

@Temperature 760 °C
 141000 psi

@Temperature 1400 °F
1195 MPa

@Temperature 650 °C
 173300 psi

@Temperature 1200 °F
Tensile Strength, Yield 910 MPa

@Strain 0.200 %
 132000 psi

@Strain 0.200 %
41.0 MPa

@Strain 0.200 %,
Temperature 1095 °C
 5950 psi

@Strain 0.200 %,
Temperature 2003 °F
135 MPa

@Strain 0.200 %,
Temperature 980 °C
 19600 psi

@Strain 0.200 %,
Temperature 1800 °F
415 MPa

@Strain 0.200 %,
Temperature 870 °C
 60200 psi

@Strain 0.200 %,
Temperature 1600 °F
770 MPa

@Strain 0.200 %,
Temperature 650 °C
 112000 psi

@Strain 0.200 %,
Temperature 1200 °F
770 MPa

@Strain 0.200 %,
Temperature 760 °C
 112000 psi

@Strain 0.200 %,
Temperature 1400 °F
Elongation at Break 26.6 %
26.6 %
in 51 mm
12 %

@Temperature 760 °C
 12 %

@Temperature 1400 °F
 in 51 mm
12 %

@Temperature 870 °C
 12 %

@Temperature 1600 °F
 in 51 mm
19.4 %

@Temperature 980 °C
 19.4 %

@Temperature 1800 °F
 in 51 mm
20.8 %

@Temperature 650 °C
 20.8 %

@Temperature 1200 °F
 in 51 mm
36.8 %

@Temperature 1095 °C
 36.8 %

@Temperature 2003 °F
 in 51 mm
Modulus of Elasticity 146 GPa

@Temperature 1000 °C
 21200 ksi

@Temperature 1830 °F
155 GPa

@Temperature 900 °C
 22500 ksi

@Temperature 1650 °F
164 GPa

@Temperature 800 °C
 23800 ksi

@Temperature 1470 °F
172 GPa

@Temperature 700 °C
 24900 ksi

@Temperature 1290 °F
180 GPa

@Temperature 600 °C
 26100 ksi

@Temperature 1110 °F
192 GPa

@Temperature 400 °C
 27800 ksi

@Temperature 752 °F
204 GPa

@Temperature 200 °C
 29600 ksi

@Temperature 392 °F
213 GPa

@Temperature 20.0 °C
 30900 ksi

@Temperature 68.0 °F
Thermal Properties Metric English Comments
CTE, linear 13.9 µm/m-°C

@Temperature 20.0 - 500 °C
 7.72 µin/in-°F

@Temperature 68.0 - 932 °F
14.3 µm/m-°C

@Temperature 20.0 - 600 °C
 7.94 µin/in-°F

@Temperature 68.0 - 1110 °F
14.8 µm/m-°C

@Temperature 20.0 - 700 °C
 8.22 µin/in-°F

@Temperature 68.0 - 1290 °F
15.4 µm/m-°C

@Temperature 20.0 - 800 °C
 8.56 µin/in-°F

@Temperature 68.0 - 1470 °F
16.4 µm/m-°C

@Temperature 20.0 - 900 °C
 9.11 µin/in-°F

@Temperature 68.0 - 1650 °F
17.8 µm/m-°C

@Temperature 20.0 - 1000 °C
 9.89 µin/in-°F

@Temperature 68.0 - 1830 °F
Thermal Conductivity 12.6 W/m-K

@Temperature 200 °C
 87.4 BTU-in/hr-ft²-°F

@Temperature 392 °F
15.7 W/m-K

@Temperature 400 °C
 109 BTU-in/hr-ft²-°F

@Temperature 752 °F
19.1 W/m-K

@Temperature 600 °C
 133 BTU-in/hr-ft²-°F

@Temperature 1110 °F
20.9 W/m-K

@Temperature 700 °C
 145 BTU-in/hr-ft²-°F

@Temperature 1290 °F
22.7 W/m-K

@Temperature 800 °C
 158 BTU-in/hr-ft²-°F

@Temperature 1470 °F
24.5 W/m-K

@Temperature 900 °C
 170 BTU-in/hr-ft²-°F

@Temperature 1650 °F
Melting Point 1330 - 1360 °C
2430 - 2480 °F
Solidus 1330 °C
2430 °F
Liquidus 1360 °C
2480 °F
Component Elements Properties Metric English Comments
Aluminum, Al 1.5 %
1.5 %
Boron, B 0.0060 %
0.0060 %
Carbon, C 0.080 %
0.080 %
Chromium, Cr 19 %
19 %
Cobalt, Co 13.5 %
13.5 %
Iron, Fe <= 2.0 %
<= 2.0 %
Manganese, Mn <= 0.10 %
<= 0.10 %
Molybdenum, Mo 4.3 %
4.3 %
Nickel, Ni 56 %
56 %
As Remainder
Silicon, Si <= 0.15 %
<= 0.15 %
Titanium, Ti 3.0 %
3.0 %
Zirconium, Zr 0.050 %
0.050 %