Micropol Microlin ML25 Linear Polyethylene Rotational Molding Powder
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Rotational Molding Grade |
| Manufacturer | Micropol Limited |
| Trade Name | Microlin |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Micropol Microlin ML25 Linear Polyethylene Rotational Molding Powder.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Micropol Limited
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D792 |
| Melt Flow | 3.0 - 4.0 g/10 min | 3.0 - 4.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | 50mm/min; ASTM D638-64T |
| Elongation at Break | 600 % | 600 % | ASTM D638-64T |
| Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D760-66 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 112 °C | 234 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
Users viewing this material also viewed the following:
- Northstar Polymers PPE-012 Curing Agent
- NOVA Chemicals Sclair® 11U4 Butene LLDPE Film Resin (discontinued **)
- Hong Kun Group 2-Adamantanamine hydrochloride Pharmaceutical Intermediate
- Huntsman IROGRAN® A 95 K 4977 TPU-High Temperature Performance
- MRC Polymers NAXELLâ„¢ PC117MH General Purpose Polycarbonate, Medium High MFR
- Taiwan Sheen Soon Sheenthane® AS-731 TPU for PU Adhesive
- SMAC SMACSONIC® Classic ST Noise and Vibration Damping
- Goodfellow Titanium 92/Silicon 8 Alloy
- Beijing Evergrow Resources PTFE Skived Sheet Tape
Copyright © lookpolymers.com All Rights Reserved