Multibase Multi-Pro® 3011 CHI Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Multi-Pro® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Pro® 3011 CHI Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Calcium Carbonate Filler, 30% by weight.Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Melt Flow | 11 g/10 min | 11 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 70 | 70 | ASTM D2240 |
| Tensile Strength, Yield | 15.2 MPa | 2200 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Flexural Yield Strength | 20.0 MPa | 2900 psi | ASTM D790 |
| Flexural Modulus | 0.931 GPa | 135 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | 73°F; ASTM D256 |
| Gardner Impact | NB | NB | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.6 °C | 195 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 188 - 216 °C | 370 - 420 °F | |
| Middle Barrel Temperature | 199 - 232 °C | 390 - 450 °F | |
| Front Barrel Temperature | 199 - 232 °C | 390 - 450 °F | |
| Nozzle Temperature | 193 - 227 °C | 380 - 440 °F | |
| Mold Temperature | 4.44 - 65.6 °C | 40.0 - 150 °F | |
| Drying Temperature | 93.3 °C | 200 °F | |
| Dry Time | 2 hour | 2 hour | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Screw Speed | 40 - 100 rpm | 40 - 100 rpm |
Users viewing this material also viewed the following:
- Polymer Resources TP-IM-G7.5 Polybutylene Terephthalate, 7.5% Glass Reinforced, Impact Modified
- PolyOne Lubri-Tech™ AT-000/8T Acetal-Copolymer, PTFE Lubricated (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP KL004AXC Acetal Homopolymer
- Unifrax Fiberfrax® QF-180™ Coating Cement
- Total MS 201 B HDPE blow molding
- A. Schulman POLYBATCH™ White 8350 EC1 Concentrate Based In LDPE
- C.O.I.M. FILCO® 657 Unsaturated Polyester Powder Resin
- CENTROPLAST BC NF Organic Thermoplastic, 15% Natural Fiber
- Axiall 1901 Clear 7002 Flexible PVC
- Teknor Apex Sinpolene MBB106LE Low Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved