PolyOne Lubri-Tech™ 5209 S2 Natural A Acetal Copolymer, 9 Melt with Silicone  (discontinued **)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Silicone Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Lubri-Tech™ 5209 S2 Natural A Acetal Copolymer, 9 Melt with Silicone  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by PolyOne™ Corporation
Physical Properties Metric English Comments
Specific Gravity 1.41 g/cc
1.41 g/cc
ASTM D792
Water Absorption 0.050 %
0.050 %
24 Hr; ASTM D570
Linear Mold Shrinkage 0.022 - 0.024 cm/cm
0.022 - 0.024 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 51.7 MPa
7500 psi
ASTM D638
Elongation at Break 45 %
45 %
ASTM D638
Tensile Modulus 2.34 GPa
340 ksi
ASTM D638
Flexural Strength 82.7 MPa
12000 psi
ASTM D790
Flexural Modulus 2.34 GPa
340 ksi
ASTM D790
Izod Impact, Notched 0.694 J/cm
1.30 ft-lb/in
ASTM D648
Thermal Properties Metric English Comments
CTE, linear 234 µm/m-°C

@Temperature 20.0 °C
 130 µin/in-°F

@Temperature 68.0 °F
 ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
ASTM D648
Processing Properties Metric English Comments
Melt Temperature 188 - 210 °C
370 - 410 °F
Mold Temperature 48.9 - 82.2 °C
120 - 180 °F
Drying Temperature 82.2 °C
180 °F