- Polykemi AB SCANAMID 66 A12^ F25 NH10 Nylon 66, Glass Fiber Reinforced, Flame Retardant
Polykemi AB SCANAMID 66 A12^ F25 NH10 Nylon 66, Glass Fiber Reinforced, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Polykemi AB |
| Trade Name | SCANAMID 66 |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANAMID 66 A12^ F25 NH10 Nylon 66, Glass Fiber Reinforced, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Filler Content | 25 % | 25 % | ±2%; Polykemi |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Modulus | 8.50 GPa @Temperature 23.0 °C |
1230 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.450 J/cm² @Temperature 23.0 °C |
2.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 249 °C | 480 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 233 °C | 451 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 226 °C @Load 5.001 kg |
439 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 248 °C @Load 1.00 kg |
478 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 1.00 mm |
V-0 @Thickness 0.0394 in |
|
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- Ineos ABS Centrex® 485 ASA+AES Blend (discontinued **)
- Huntsman Araldite GT 7074 Bisphenol A Epoxy Solid Resin
- MarkeTech Repton 868 Zirconia + 8 mol% Yttria (YSZ)
- Lord Adhesives Flocklok® 870 Flock Adhesive
- Latrobe Lescalloy® 16NCD13 VAC-ARC High Strength Alloy Steel
- H.C. Starck Grade B Zirconium Diboride, ZrB2
- A. Schulman POLYBATCH™ Green 3251V Concentrate Based In Polyethylene
- DSM Akulon® K223-TP4 Impact Modified Nylon 6 (European and Asian Grade) (Dry)
- Azoty Tarnow™ Tarnamid® T-27 GF10 MX6 Polyamide 6 - Flame Retarded, Reinforced
- Saint-Gobain Rulon® FCJ Grade Bearing/Seal PTFE (discontinued **)
Copyright © lookpolymers.com All Rights Reserved