Polykemi AB SCANAMID 66.6 C22^E F Nylon 66/6, Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 |
| Manufacturer | Polykemi AB |
| Trade Name | SCANAMID 66.6 |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANAMID 66.6 C22^E F Nylon 66/6, Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 75.0 MPa | <= 10900 psi | ISO/R527 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO/R527 |
| Flexural Strength | <= 120 MPa | <= 17400 psi | ISO 178 |
| Flexural Modulus | 2.80 GPa @Temperature 23.0 °C |
406 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | >= 195 °C @Load 5.001 kg |
>= 383 °F @Load 11.03 lb |
50°C/h; ISO 306 |
Users viewing this material also viewed the following:
- Polymer Resources PC-FR3A-D Polycarbonate, Flame Retardant, High Flow
- Shin-Etsu Silicones X-33-514 Silicone Primer
- Unipetrol Heavy Oil Hydrogenate
- A. Schulman SCHULAMID® 6 GF15H 30% Glass Fiber Reinforced Nylon 6
- Clariant Renol PA213G13 Nylon 6, 13% Glass Fiber, Heat Stabilized, Lubricated
- E-Polymers TEKANATE® G7007 Extrusion Injection Molding Polycarbonate
- REXtac Rextac® RT 5224 Amorphous Polyalphaolefin (APAO)
- BP Amoco Acclear® 8949 Random Copolymer Polypropylene, High Clarity Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved