Polyram PlusTek PA355M6 Nylon 6.6 for Injection Molding, 30% Mineral Filled, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Mineral Filled
Manufacturer Polyram
Trade Name PlusTek
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polyram PlusTek PA355M6 Nylon 6.6 for Injection Molding, 30% Mineral Filled, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
30% Minerals filled, flame retardant Nylon 6.6 for injection molding applications.Information provided by Polyram.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 1.8 %
1.8 %
50% RH; ISO 62
Water Absorption at Saturation 5.5 %
5.5 %
ISO 62
Linear Mold Shrinkage 0.0080 - 0.012 cm/cm
0.0080 - 0.012 in/in
ISO 2577
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
Tensile Strength, Yield 80.0 MPa
11600 psi
ISO 527
Elongation at Break 5.0 %
5.0 %
ISO 527
Flexural Strength 130 MPa
18900 psi
ISO 178
Flexural Modulus 4.50 GPa
653 ksi
ISO 178
Izod Impact, Notched (ISO) 5.50 kJ/m²
2.62 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Melting Point 256 °C
493 °F
ISO 11357
Maximum Service Temperature, Air 80.0 °C
176 °F
Continuous use
220 °C
428 °F
Short peaks operation
Deflection Temperature at 0.46 MPa (66 psi) 235 °C
455 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 145 °C
293 °F
ISO 75
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz
 3.7

@Frequency 1.00e+6 Hz
 IEC 60250
Dielectric Strength 85.0 kV/mm
2160 kV/in
IEC 60250