- Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled
- Samsung Cheil Industries Starex® VG-4910 ABS, Glass Filled FR
Samsung Cheil Industries Starex® VG-4910 ABS, Glass Filled FR
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® VG-4910 ABS, Glass Filled FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 23 g/10 min @Load 10.0 kg, Temperature 220 °C |
23 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength at Break | 75.5 MPa | 11000 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 73.5 MPa | 10700 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 3.4 % | 3.4 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.73 GPa | 540 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 78.5 MPa | 11400 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 3.63 GPa | 526 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 0.686 J/cm @Thickness 3.17 mm |
1.29 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| 1.18 J/cm @Thickness 6.35 mm |
2.20 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C @Thickness 6.40 mm |
216 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C @Thickness 6.40 mm |
207 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | B/50; ISO R306 |
| 101 °C | 214 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-0 @Thickness 1.60 - 3.00 mm |
V-0 @Thickness 0.0630 - 0.118 in |
|
| 5VB @Thickness 2.50 mm |
5VB @Thickness 0.0984 in |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Enviramid™ N2300HL BK Post Consumer Recycle Nylon 6
- Eastman D4028-F Polyethylene (discontinued **)
- Lehmann & Voss LUVOCOM® 1700-8541 PPO, unreinforced
- LG Chemical LUMAX HF-5306F High Flow PBT, 30% Polymer Alloy, Weather Resistant, Flame Retardant
- LyondellBasell Hifaxâ„¢ HSBMG265 Thermoplastic Polyolefin Elastomer
- SABIC Innovative Plastics LNP STAT-KON Noryl_FMC3008A PPE+HIPS (Europe-Africa-Middle East)
- Lubrizol Estane® T465A Thermoplastic Polyurethane
- CoorsTek PolyGlyde™ 2000 Self-Lubricating Seal
- Abatron AboCast/AboCure 8109-8
- C.O.I.M. UREXTER® Lp 285 Polyurethane Two-Component Compound
Copyright © lookpolymers.com All Rights Reserved