Shinkong Synthetic Fibers Shinite® N602G6S Nylon 66, Fire Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Shinkong Synthetic Fibers Corp |
| Trade Name | Shinite® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Shinkong Synthetic Fibers Shinite® N602G6S Nylon 66, Fire Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information from Shinkong Synthetic Fibers Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.67 g/cc | 1.67 g/cc | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.012 - 0.015 cm/cm | 0.012 - 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 137 MPa | 19900 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 206 MPa | 29900 psi | ASTM D790 |
| Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
| Izod Impact, Notched | 0.883 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.65 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
Users viewing this material also viewed the following:
- MV Labs LA870 La2(C2O4)3·xH2O Lanthanum oxalate hydrate
- Nabaltec GRANALOX® NM 9916 F Ceramic Body
- LyondellBasell Alathon® L5485 High Density Polyethylene
- Saint-Gobain CHR® G569 Glass Cloth Backing Acrylic Adhesive Pressure Sensitive Tape
- Zotefoams Evazote® VA25 Ethylene Vinyl Acetate Copolymer Foam
- Elektro-Isola G-Etronax EP 215 S Epoxy, Glass Fabric Reinforcement, Green, Sheets
- Addcomp PRIEX® 12031 Maleic Anhydride Grafted HDPE
- Arlon 49442R0075EP 0.0075" (0.190 mm) Cured Silicone Rubber with Fiberglass Substrate
- Alliance N-30UH Neodymium Iron Boron Magnetic Material
- Techmer ES HiFill FR® PA6 GF15 FR HS L 15% Glass Filled
Copyright © lookpolymers.com All Rights Reserved