Solvay Specialty Polymers Amodel® A-4160 HSL Polyphthalamide (PPA), 60% Glass Fiber

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer Solvay Specialty Polymers
Trade Name Amodel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® A-4160 HSL Polyphthalamide (PPA), 60% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel® A-4160 HSL resin is a 60% glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits high modulus at elevated temperatures, a high heat deflection temperature and exceptional creep resistance. This material was designed for metal replacement applications. Its rapid crystallization and good flow characteristics allow shorter cycles for enhanced molding productivity.Features: Fast Molding Cycle; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Toughness; Heat Stabilized; High Heat Resistance; High Strength; Hot Water Moldability; Low CLTE; Lubricated; Ultra High StiffnessUses: Automotive Applications; Automotive Electronics; Automotive Under the Hood; Camera Applications; Cell Phones; Connectors; Electrical/Electronic Applications; Housings; Industrial Applications; Machine/Mechanical Parts; Metal Replacement; Transmission ApplicationsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Automotive Specifications ASTM D6779 PA102G60Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.75 g/cc
0.0632 lb/in³
ISO 1183
Filler Content 60 %
60 %
Glass Fiber
Water Absorption 0.19 %

@Time 86400 sec
0.19 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 79.6 MPa

@Temperature 200 °C
11500 psi

@Temperature 392 °F
2; ISO 527-2
244 MPa

@Temperature 23.0 °C
35400 psi

@Temperature 73.4 °F
2; ISO 527-2
Elongation at Break 1.4 %

@Temperature 23.0 °C
1.4 %

@Temperature 73.4 °F
ISO 527-2
3.3 %

@Temperature 200 °C
3.3 %

@Temperature 392 °F
ISO 527-2
Tensile Modulus 8.77 GPa

@Temperature 200 °C
1270 ksi

@Temperature 392 °F
2; ISO 527-2
23.3 GPa

@Temperature 23.0 °C
3380 ksi

@Temperature 73.4 °F
2; ISO 527-2
Flexural Strength 137 MPa

@Temperature 200 °C
19900 psi

@Temperature 392 °F
2; ISO 178
385 MPa

@Temperature 23.0 °C
55800 psi

@Temperature 73.4 °F
2; ISO 178
Flexural Modulus 8.50 GPa

@Temperature 200 °C
1230 ksi

@Temperature 392 °F
ISO 178
19.3 GPa

@Temperature 23.0 °C
2800 ksi

@Temperature 73.4 °F
ISO 178
Charpy Impact Unnotched 13.0 J/cm²
61.9 ft-lb/in²
Type 1, Edgewise; ISO 179
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
Type 1, Edgewise; ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 304 °C
579 °F
Unannealed; ISO 75-2/A
Processing Properties Metric English Comments
Rear Barrel Temperature 318 - 324 °C
604 - 615 °F
Front Barrel Temperature 327 - 332 °C
621 - 630 °F
Melt Temperature 329 - 343 °C
624 - 649 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 120 °C

@Time 14400 sec
248 °F

@Time 4.00 hour
Descriptive Properties Value Comments
Additive Heat Stabilizer
Lubricant
Mold Release
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black
Form Pellets
Processing Technique Water-Heated Mold Injection Molding
RoHS Compliance RoHS Compliant