Special Metals INCOLOY® Alloy 800HT™
| Category | Metal , Superalloy , Iron Base |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCOLOY® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCOLOY® Alloy 800HT™.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A nickel-iron-chromium alloy having the same basic composition as INCOLOY alloy 800 but with significantly higher creep-rupture strength. The higher strength results from close control of the carbon, aluminum, and titanium contents in conjunction with a high-temperature anneal. Used in chemical and petrochemical processing, in power plants for super-heater and reheater tubing, in industrial furnaces, and for heat-treating equipment. Standard product forms are round, flats, forging stock, pipe, tube, plate, sheet, strip, and wire.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.94 g/cc | 0.287 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 560 MPa | 81200 psi | Annealed |
| 480 MPa @Temperature 550 °C |
69600 psi @Temperature 1020 °F |
Annealed prior to test | |
| Tensile Strength, Yield | 250 MPa | 36300 psi | Annealed |
| 130 MPa @Temperature 550 °C |
18900 psi @Temperature 1020 °F |
Annealed prior to test | |
| Elongation at Break | 45 % | 45 % | Annealed prior to test. |
| 44 % @Temperature 550 °C |
44 % @Temperature 1020 °F |
Annealed prior to test. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 - 100 °C |
8.00 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Specific Heat Capacity | 0.460 J/g-°C | 0.110 BTU/lb-°F | |
| Thermal Conductivity | 11.5 W/m-K | 79.8 BTU-in/hr-ft²-°F | |
| Melting Point | 1357 - 1385 °C | 2475 - 2525 °F | |
| Solidus | 1357 °C | 2475 °F | |
| Liquidus | 1385 °C | 2525 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 0.15 - 0.60 % | 0.15 - 0.60 % | |
| Carbon, C | 0.060 - 0.10 % | 0.060 - 0.10 % | |
| Chromium, Cr | 19 - 23 % | 19 - 23 % | |
| Copper, Cu | <= 0.75 % | <= 0.75 % | |
| Iron, Fe | >= 39.5 % | >= 39.5 % | |
| Manganese, Mn | <= 1.5 % | <= 1.5 % | |
| Nickel, Ni | 30 - 35 % | 30 - 35 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.015 % | <= 0.015 % | |
| Titanium, Ti | 0.15 - 0.60 % | 0.15 - 0.60 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000989 ohm-cm | 0.0000989 ohm-cm | |
| Magnetic Permeability | 1.014 | 1.014 | at 200 oersted (15.9 kA/m) |
| Curie Temperature | -115 °C | -175 °F |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ FR WC 0587-21 R2 RoHS Polypropylene, Unspecified (PP, Unspecified)
- Isoflon Tisoflon® 14G Polytetrafluoroethylene & Graphite Coated Glass Fabric
- A. Schulman FORMION™ FI 232H 10% Mineral Reinforced Ionomer / Nylon Alloy
- Borealis MS64T20 Polypropylene Compound, Mineral Filled
- ExxonMobil Bicor® 60 CSR-2 OPP Film
- ExxonMobil Santoprene® 691-73W175 Thermoplastic Vulcanizate
- E-Polymers TEKAMID® TA250G45 , 45% Glass Fiber Reinforced PA66, DAM
- Fainplast Compounds CKL 79 Flexible PVC, Sheathing Lead Free
- Henkel Turco 5668 Landing Gear Cleaner
Copyright © lookpolymers.com All Rights Reserved