Sumitomo Chemical Sumipex® LG35 Acrylic Resin, High Flow
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, High Flow, Molded |
| Manufacturer | Sumitomo Chemical |
| Trade Name | Sumipex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Chemical Sumipex® LG35 Acrylic Resin, High Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product CharacteristicsHigh FlowImproved Cycle TimeInformation provided by Calsak Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 35 g/10 min @Load 3.80 kg, Temperature 230 °C |
35 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.7 MPa | 8800 psi | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Yield Strength | 103 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 2.90 GPa | 420 ksi | ASTM D790 |
| Izod Impact, Notched | 0.160 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
0.300 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 83.9 °C @Thickness 3.17 mm |
183 °F @Thickness 0.125 in |
annealed; ASTM D648 |
| Vicat Softening Point | 95.0 °C | 203 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.49 | 1.49 | ASTM D542 |
| Haze | 0.50 % | 0.50 % | ASTM D1003 |
| Transmission, Visible | 93 % | 93 % | Total light Transmission; ASTM D1003 |
Users viewing this material also viewed the following:
- ExxonMobil LL 3402.48 Cast Film Resin (discontinued **)
- Lanxess Pocan® KU 2-7503/1 000000 PBT
- Lehigh Technologies 80 Mesh Ground Reclaimed Whole Tire Rubber
- A. Schulman ComAlloy® E-14756 Flame Retardant Easy Flow Polycarbonate Alloy
- BASF Elastollan C 75 A HPM TPUR
- ATI Allegheny Ludlum D2 Tool Steel, UNS T30402
- 3M 2A12 (Clear) Co-Extruded Polyethylene Protective Tapes
- Multibase Multibatch® MP 63001 Anti-split
- Gromax CFG33-QS11N1 Nylon 6 33% Glass Filled (Dry)
Copyright © lookpolymers.com All Rights Reserved