Polymer Property : Density = 1.02 g/cc Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Density 1.02 g/cc
0.0368 lb/in³
Finaprene 2602 Method
Total Finaclear® 530 Clear Impact Polystyrene  (discontinued **)
Finaclear® 530 is a clear high styrenic styrene-butadiene (SBS) elastomer, providing dramatically improved impact properties and tear resistance to finished articles, when used in blends with other..
Density 1.02 - 1.02 g/cc

@Temperature 280 - 300 °C
0.0368 - 0.0368 lb/in³

@Temperature 536 - 572 °F
Average value: 1.02 g/cc Grade Count:6
Overview of materials for Polycarbonate, Impact Modified
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Impact Modified". Each property range of values reported is minimum and maximum values of..
Density 1.02 - 1.14 g/cc
0.0368 - 0.0411 lb/in³
Lord Adhesives 18 Mix-In Accelerator for use with all Lord Acrylic Adhesives
Lord Adhesives 18 Mix-In Accelerator for use with all Lord Acrylic AdhesivesLord Accelerator 18 Black Mix-In Accelerator for use with all Lord Acrylic Adhesives. May be used at ratios from 2:1 throu..
Density 1.02 g/cc
0.0368 lb/in³
ISO 1183
LyondellBasell Hostacomâ„¢ TSOP-UM5 Thermoplastic Polyolefin Elastomer
Description: Hostacomâ„¢ TSOP-UM5 high melt flow, 2,000 MPa flexural modulus, natural, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent balance of properties and proce..
Density 1.02 g/cc
0.0368 lb/in³
ASTM D792
Techmer ES HiFill® PP GF15 CC 15% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightFeatures: Chemically CoupledInformation provided by TP Composites, Inc.
Density 1.02 g/cc
0.0368 lb/in³
ASTM D792
Techmer ES Plastiblend® ABS 8010
Availability: North AmericaForms: PelletsProcessing Method: Extrusion Blow Molding and Sheet ExtrusionInformation provided by TP Composites, Inc.
Density 1.02 g/cc
0.0368 lb/in³
ASTM D792
UBE UBESTA® 3024LU Rigid Black Electronic Grade Nylon 12
Description: UBESTA Nylon 12 has an excellent termite resistance than other plastics. UBESTA contributes as a material for jacket and sheath which lay for telephone and telegram Communication System..
Density 1.02 g/cc
0.0368 lb/in³
ASTM D792 - ISO 1183
DuPont Elvaloy® 742 Ethylene/Vinyl Acetate/Carbon Monoxide Copolymer
Specialized copolymers deliver flexibility, toughness and weatherability to adhesives, plastics, highways and roofing.Availability: GloballyInformation provided by DuPont.
Density 1.02 g/cc
0.0368 lb/in³
ISO 1183
Polyplastics TOPAS® 5013 Cyclic Olefin Copolymer (COC) (Asia/Pacific Grade)
This grade is characterized by its high flowability and superior optical properties. It is suitable for optical components such as lenses and light guide panels where high molded precision is indisp..
Density 1.02 g/cc
0.0368 lb/in³
ISO 1183
Topas Advanced Polymers TOPAS® 5013S-04 Cyclic Olefin Copolymer (COC)
TOPAS® 5013S-04 is a high flow injection molding grade with a 130°C heat distortion temperature. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high ..
Density 1.02 g/cc
0.0368 lb/in³
ISO 1183
Topas Advanced Polymers TOPAS® 9506F-500 Cyclic Olefin Copolymer (COC)
TOPAS® 9506F-500 is a high clarity extrusion grade for use in shrink, food and medical packaging as either a discrete layer in multilayer film or in blends with polyethylene. It is designed to del..
Density 1.02 g/cc
0.0368 lb/in³
ASTM D792
UBE UBESTA® 3035LU1 Rigid Piping Grade Nylon 12
Description: UBESTA contributes to the field of Utilities such as plastic pipe system evolutionary developed for gas industry. It is used for both burial and for rehabilitation of existing cast iron..
Density 1.02 g/cc
0.0368 lb/in³
ASTM D792
Chevron Phillips K-Resin® XK40 Styrene-Butadiene Copolymer, Sheet Grade
Styrene-Butadiene CopolymerCustomer Benefits: XK40 is an extrusion grade SBC designed specifically for superior performance in blends with general purpose polystyrene. Compared to KK38, KX40 offers..
Density 1.02 g/cc
0.0368 lb/in³
Melt
Covestro Desmopan® 481 Polyurethane
injection molding gradefree from plasticizersgrease and oil-resistantlow compression sethigh elasticitygood heat resistanceEasy releaseApplicationRoller coatingSealsmembranesAutomotive engineeringPr..
Density 1.02 g/cc
0.0368 lb/in³
Melt
Covestro Desmopan® DP 1485A Polyurethane
Extrusion- and injection molding gradesuitable for extrusion blow moldingvery large processing windowhigh melt stabilityBeadsApplicationBellowsHosesnon-reinforcedProfilesInjection molded engineering..
Density 1.02 g/cc
0.0368 lb/in³
Melt
Covestro Desmopan® DP 3660DU Polyurethane
Extrusion- and injection molding gradetransparent up to 6 mm wall thicknesshydrolysis-stabilisedwith special UV stabilizerswith release agentgood wear resistanceApplicationSports shoe solesHosesnon-..
Density 1.02 g/cc
0.0368 lb/in³
Melt
Covestro Desmopan® DP 3695AU Polyurethane
Extrusion- and injection molding gradetransparent up to 6 mm wall thicknesshydrolysis-stabilisedwith special UV stabilizerswith release agentgood wear resistanceApplicationSports shoe solesHosesnon-..
Density 1.02 g/cc

@Temperature 260 °C
0.0368 lb/in³

@Temperature 500 °F
Melt
Covestro Makroblend® DP UT3907 Polycarbonate + PBT, Impact Grade
Developmental product(PC+PBT)-blendhigh flowimpact modifiedeasy releaseUV-stabilizedinjection molding grade Makroblend DP UT3907* offers superior flowability, good impact strength and excellent ch..
Density 1.02 g/cc

@Temperature 300 °C
0.0368 lb/in³

@Temperature 572 °F
Melt
Covestro Makrolon® Rx1805 Polycarbonate
ISO 7391-PC,M,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minMedical devicesLipid resistantsuitable for sterilization with high-energy radiationComplies with the requirements of FDA-modifie..
Density 1.02 g/cc
0.0368 lb/in³
ASTM D792, ISO 1183
DuPont™ Appeel® 20D828 Ethylene Acrylate
Appeel® 20D828 is an modified ethylene acrylate resin designed to function as a sealing layer for lidding applications. It is most often suggested to provide strong peelable seals over a broad temp..
Density 1.02 g/cc
0.0368 lb/in³
Dow Latex LXC 8476NA Carboxylated Styrene-Butadiene Latex
Applications: Latex LXC 8476NA is the “industry standard” in the Styron product line. Latex LXC 8476NA is an ammonia-free product specifically designed for residential carpet or higher-load commer..
Density 1.02 g/cc

@Temperature 300 °C
0.0368 lb/in³

@Temperature 572 °F
Melt
Covestro Makrolon® 1243 Polycarbonate
ISO 7391-PC,ELS,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minExtrusionHigh viscosityBranchedUV stabilizedEasy releaseAvailable in color code 550111onlyMulti wall sheet/profilesPreprocessi..
Density 1.02 g/cc
0.0368 lb/in³
ISO 1183
Arkema Group Pebax® MV 3000 SP 01 Polyether Block Amide (PEBA)
Polyether block amide PEBAX® MV 3000 SP 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This hydrophilic grade when extruded into either a thin film or laminated on ..
Density 1.02 g/cc
0.0368 lb/in³
Arkema Group Rilsan® AMN P20 TLD Nylon 12, Flexible, Injection Grade (Conditioned)
Designation ISO 1874-PA12-P,MHLR,14-005Flexible grade for injection molding. Available colors: black and natural. Light and heat stabilized. Mold-release agent.Good impact strength. Flexibility and ..
Density 1.02 g/cc
0.0368 lb/in³
ISO 1183
Arkema Group Pebax® Clear 400 Polyether Block Amide (PEBA)
Pebax® Clear 400 combines high transparency level with the unique performance of Pebax®, thermoplastic elastomer made of flexible polyether and rigid polyamide.Information provided by Arkema Group..
Density 1.02 g/cc

@Temperature 260 °C
0.0368 lb/in³

@Temperature 500 °F
Melt
Covestro Makroblend® DP UT6007 Polycarbonate + PBT, Impact Grade
Developmental product(PC+PBT)-blendimpact modifiedeasy releaseUV-stabilizedinjection molding grade Makroblend DP UT6007* offers an exceptional low-temperature impact strength, good flowability and..