Arkema Group Pebax® Rnew 35R53 SP 01 Polyether Block Amide (PEBA)

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyether Block Amide (PEBA)
Manufacturer Arkema
Trade Name Pebax®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Pebax® Rnew 35R53 SP 01 Polyether Block Amide (PEBA).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyether block amide Pebax® 35R53 SP 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide based on renewable resources. This SP grade has been developed to be heat and UV resistant.Information provided by Arkema Group
Physical Properties Metric English Comments
Density 1.02 g/cc
0.0368 lb/in³
ISO 1183
Water Absorption 1.3 %

@Temperature 23.0 °C,
Time 86400 sec
1.3 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 0.50 %

@Temperature 20.0 °C
0.50 %

@Temperature 68.0 °F
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0060 cm/cm

@Thickness 4.00 mm,
Time 86400 sec
0.0060 in/in

@Thickness 0.157 in,
Time 24.0 hour
Linear Mold Shrinkage, Transverse 0.0060 cm/cm

@Thickness 4.00 mm,
Time 86400 sec
0.0060 in/in

@Thickness 0.157 in,
Time 24.0 hour
Mechanical Properties Metric English Comments
Hardness, Shore D 32
32
Instantaneous, Conditioned 15 days at 23°C - 50% RH; ISO 868
25

@Time 15.0 sec
25

@Time 0.00417 hour
Conditioned 15 days at 23°C - 50% RH; ISO 868
Tensile Strength at Break 30.0 MPa
4350 psi
Conditioned 15 days at 23°C - 50% RH; ASTM D638
Elongation at Break >= 700 %
>= 700 %
Conditioned 15 days at 23°C - 50% RH; ASTM D638
Flexural Modulus 0.0400 GPa
5.80 ksi
Conditioned 15 days at 23°C - 50% RH; ISO178
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 135 °C
275 °F
ISO 11357
Vicat Softening Point 81.0 °C

@Load 1.02 kg
178 °F

@Load 2.25 lb
ISO 306
Component Elements Properties Metric English Comments
Carbon, C 28 - 32 %
28 - 32 %
Renewable; ASTM 6866
Processing Properties Metric English Comments
Processing Temperature 205 °C
401 °F
Recommended Extrusion Temperature
190 - 220 °C
374 - 428 °F
Extrusion Range
Nozzle Temperature 180 - 240 °C
356 - 464 °F
210 °C
410 °F
Recommended
Mold Temperature 10.0 - 30.0 °C
50.0 - 86.0 °F
Drying Temperature 55.0 - 65.0 °C
131 - 149 °F
Dry Time 4.00 - 8.00 hour
4.00 - 8.00 hour