Polymer Property : Linear Mold Shrinkage, Transverse = 0.011 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC LNP* Lubricomp* DBL32 is a compound based on Polycarbonate resin containing 10% Glass Beads and 15% PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DL001 PC LNP* LUBRICOMP* DL001 is a compound based on Polycarbonate resin containing 5% PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DL001 PC (Asia Pacific) LNP* Lubricomp* DL001 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DL003P PC LNP LUBRICOMP* DL003P is a compound based on Polycarbonate resin containing 15% PTFE. Added features of this material include: Exceptional Processing, Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DL003P PC (Asia Pacific) LNP LUBRICOMP* DL003P is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Exceptional Processing.
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP DL003P PC (Asia Pacific) LNP LUBRICOMP* DL003P is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Exceptional Processing.
Linear Mold Shrinkage, Transverse	0.0080 - 0.011 cm/cm @Time 86400 sec	0.0080 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing 15% PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0080 - 0.011 cm/cm @Time 86400 sec	0.0080 - 0.011 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI (Asia Pacific) LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0080 - 0.011 cm/cm @Time 86400 sec	0.0080 - 0.011 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI (Europe-Africa-Middle East) LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0080 - 0.011 cm/cm @Thickness 3.20 - 4.60 mm	0.0080 - 0.011 in/in @Thickness 0.126 - 0.181 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 855 PBT 15% GR PBTP, UL94 V-0 rated. Improved surface appearance. For external housings: steam irons, appliance housings and lighting parts.
Linear Mold Shrinkage, Transverse	0.0080 - 0.011 cm/cm @Thickness 3.20 - 4.60 mm	0.0080 - 0.011 in/in @Thickness 0.126 - 0.181 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 855 PBT (Asia Pacific) 15% GR PBTP, UL94 V-0 rated. Improved surface appearance. For external housings: steam irons, appliance housings and lighting parts.
Linear Mold Shrinkage, Transverse	0.0080 - 0.011 cm/cm @Thickness 3.20 - 4.60 mm	0.0080 - 0.011 in/in @Thickness 0.126 - 0.181 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® DR48 PBT 17% glass reinforced, flame retardant grade UL-94 rated V-0/5VA.
Linear Mold Shrinkage, Transverse	0.0080 - 0.011 cm/cm @Thickness 3.20 - 4.60 mm	0.0080 - 0.011 in/in @Thickness 0.126 - 0.181 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® DR48 PBT (Asia Pacific) 17% glass reinforced, flame retardant grade UL-94 rated V-0/5VA.
Linear Mold Shrinkage, Transverse	0.0080 - 0.011 cm/cm @Thickness 3.20 - 4.60 mm	0.0080 - 0.011 in/in @Thickness 0.126 - 0.181 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® DR51 PBT (Asia Pacific) 15% GR polyester, excellent mechanical, thermal and electrical performance. Non-flame retardant. Spotlights, appliance housings, handles, connectors
Linear Mold Shrinkage, Transverse	0.0080 - 0.011 cm/cm @Thickness 3.20 - 4.60 mm	0.0080 - 0.011 in/in @Thickness 0.126 - 0.181 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® DR51M PBT (Asia Pacific) 15% GR; exc. mechanical/thermal/electrical performance; nonflame retardant. For spotlights, appliance housings, handles. Easy flow/int. mold release.This data was supplied by SABIC-IP for the Asia ..
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-KON WE002 PBT LNP STAT-KON* WE002 is a compound based on PBT resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-KON WE002 PBT (Asia Pacific) LNP STAT-KON* WE002 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS LNP* STAT-LOY* AF3009 is a compound based on ABS resin containing 10% Glass Fiber. Added features of this material include: Antistatic, Flame Retardant.
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS (Asia Pacific) LNP* Stat-loy* AF3009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Antistat, Flame Retardant.
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP IX04513C PA 6/12 (Asia Pacific) LNP THERMOCOMP* IX04513C is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Clean Compounding System.
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP MF006S PP LNP* THERMOCOMP* MF006S is a compound based on Polypropylene resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized.
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp OF004AER PPS LNP* Thermocomp* OF004AER is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.This data was supplied by SA..
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP RF006EXZ PA 66 LNP THERMOCOMP* RF006EXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Easy Molding.
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOTUF QX01581H PA6.10 LNP THERMOTUF* QX01581H is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: High Impact.
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOTUF QX01581H PA6.10 LNP THERMOTUF* QX01581H is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: High Impact.
Linear Mold Shrinkage, Transverse	0.0080 - 0.011 cm/cm @Thickness 3.20 - 4.60 mm	0.0080 - 0.011 in/in @Thickness 0.126 - 0.181 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 451E PBT 20% GR. Easy flow version of VALOX 451.
Linear Mold Shrinkage, Transverse	0.010 - 0.011 cm/cm @Time 86400 sec	0.010 - 0.011 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP IF003 PA 6/12 LNP THERMOCOMP* IF003 is a compound based on Nylon 6/12 resin containing 15% Glass Fiber.
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp OF002A PPS LNP* Thermocomp* OF002A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP RF006ESZ PA 66 LNP THERMOCOMP* RF006ESZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOTUF QX01581H PA 6/10 (Asia Pacific) LNP* THERMOTUF* QX01581H is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: High Impact.