SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Stat-loy
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-LOY* AF3009 is a compound based on ABS resin containing 10% Glass Fiber. Added features of this material include: Antistatic, Flame Retardant.
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ASTM D792
1.31 g/cc
0.0473 lb/in³
ISO 1183
Moisture Absorption 2.00 %
2.00 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0080 - 0.010 cm/cm

@Time 86400 sec
 0.0080 - 0.010 in/in

@Time 24.0 hour
 ASTM D955
0.0093 cm/cm

@Time 86400 sec
 0.0093 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0090 - 0.011 cm/cm

@Time 86400 sec
 0.0090 - 0.011 in/in

@Time 24.0 hour
 ASTM D955
0.010 cm/cm

@Time 86400 sec
 0.010 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 42.0 MPa
6090 psi
ASTM D638
42.0 MPa
6090 psi
ISO 527
Tensile Strength, Yield 42.0 MPa
6090 psi
ASTM D638
43.0 MPa
6240 psi
ISO 527
Elongation at Break 1.8 %
1.8 %
ISO 527
1.9 %
1.9 %
ASTM D638
Elongation at Yield 1.8 %
1.8 %
ASTM D638
1.8 %
1.8 %
ISO 527
Tensile Modulus 3.62 GPa
525 ksi
1 mm/min; ISO 527
4.13 GPa
599 ksi
50 mm/min; ASTM D638
Flexural Strength 55.0 MPa
7980 psi
ASTM D790
61.0 MPa
8850 psi
ISO 178
Flexural Modulus 3.20 GPa
464 ksi
ISO 178
3.44 GPa
499 ksi
ASTM D790
Izod Impact, Notched 0.320 J/cm
0.599 ft-lb/in
ASTM D256
Izod Impact, Unnotched 2.24 J/cm
4.20 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 4.00 J
2.95 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 93.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 52.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
94.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 52.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 61.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 34.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
62.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 34.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 98.0 °C
208 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
96.0 °C

@Thickness 3.20 mm
 205 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
87.0 °C

@Thickness 3.20 mm
 189 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94 by SABIC-IP
Electrical Properties Metric English Comments
Surface Resistance 1.00e+10 - 1.00e+12 ohm
1.00e+10 - 1.00e+12 ohm
ASTM D257