- Polymer Property : Linear Mold Shrinkage = 0.019 cm/cm
Polymer Property : Linear Mold Shrinkage = 0.019 cm/cm Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage | 0.013 - 0.019 cm/cm | 0.013 - 0.019 in/in | ISO 294-4 |
| Premix Thermoplastics PRE-ELEC® PP 1391 Conductive Thermoplastic Compound PRE-ELEC® PP 1391 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-E.. |
|||
| Linear Mold Shrinkage | 0.013 - 0.019 cm/cm | 0.013 - 0.019 in/in | ISO 294-4 |
| Premix Thermoplastics PRE-ELEC® PP 1397 Conductive Thermoplastic Compound PRE-ELEC® PP 1397 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-E.. |
|||
| Linear Mold Shrinkage | 0.0090 - 0.019 cm/cm | 0.0090 - 0.019 in/in | FRISETTA Test Method |
| Nilit FRIANYL B63 SG-GV 2515 Nylon 6 for injection molding, 25% mineral filled and 15% glass fiber reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Linear Mold Shrinkage | 0.0090 - 0.019 cm/cm | 0.0090 - 0.019 in/in | FRISETTA Test Method |
| Nilit FRIANYL B63 SG-GV 2010 Nylon 6 for injection molding, 20% mineral filled and 10% glass fiber reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Linear Mold Shrinkage | 0.012 - 0.019 cm/cm | 0.012 - 0.019 in/in | |
| Lehmann & Voss LUVOCOM® 19-7950 Polyamide 46, with aramid reinforcement and PTFE, toughness-modified, easy flowing Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Good friction and wear behaviour especially at increased temperatures.Emergency running propert.. |
|||
| Linear Mold Shrinkage | 0.016 - 0.019 cm/cm | 0.016 - 0.019 in/in | ASTM D955 |
| LG Chemical LUCEL MR-310 Low Warpage POM, 10% Mineral Filled LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
| Linear Mold Shrinkage | 0.018 - 0.019 cm/cm | 0.018 - 0.019 in/in | ASTM D955 |
| Kolon KOPA® KN170SA General Purpose Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
| Linear Mold Shrinkage | 0.016 - 0.019 cm/cm | 0.016 - 0.019 in/in | ASTM D955 |
| Kolon KOPA® KN333HI5BL High Impact Nylon 66 Middle viscosity, Impact -resistantApplications A variety of fuse boxes, relax boxesInformation provided by API-Kolon. |
|||
| Linear Mold Shrinkage | 0.016 - 0.019 cm/cm | 0.016 - 0.019 in/in | ASTM D955 |
| Kolon KOPA® KN333NW High Impact Nylon 66 Impact -resistant, dimensional safetyApplications Wheel coversInformation provided by API-Kolon. |
|||
| Linear Mold Shrinkage | 0.015 - 0.019 cm/cm | 0.015 - 0.019 in/in | ASTM D955 |
| Kolon SPESIN® KP513 PBT Alloy Resin Excellent extrudable and SpinningApplications: Mono filamentInformation provided by API-Kolon. |
|||
| Linear Mold Shrinkage | 0.015 - 0.019 cm/cm | 0.015 - 0.019 in/in | ASTM D955 |
| Kolon SPESIN® KP515FLBL High Impact PBT Alloy Resin High elastic, whether resistantApplications: WipersInformation provided by API-Kolon. |
|||
| Linear Mold Shrinkage | 0.013 - 0.019 cm/cm | 0.013 - 0.019 in/in | ASTM D955 |
| Kolon Kopa® KN138R Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |
|||
| Linear Mold Shrinkage | 0.011 - 0.019 cm/cm @Thickness 3.20 mm |
0.011 - 0.019 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
| A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy DescriptionFormion® FI 241E is a patented non-reinforced, extrusion grade Ionomer alloy. It has bee formulated for high durability, low gloss, and low temperature ductility.ApplicationFormion® FI.. |
|||
| Linear Mold Shrinkage | 0.011 - 0.019 cm/cm @Thickness 3.20 mm |
0.011 - 0.019 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
| A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy DescriptionFormion® FI 241E is a patented non-reinforced, extrusion grade Ionomer alloy. It has bee formulated for high durability, low gloss, and low temperature ductility.ApplicationFormion® FI.. |
|||
| Linear Mold Shrinkage | 0.011 - 0.019 cm/cm @Thickness 3.20 mm |
0.011 - 0.019 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
| A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy DescriptionFormion® FI 241E is a patented non-reinforced, extrusion grade Ionomer alloy. It has bee formulated for high durability, low gloss, and low temperature ductility.ApplicationFormion® FI.. |
|||
| Linear Mold Shrinkage | 0.015 - 0.019 cm/cm | 0.015 - 0.019 in/in | |
| Polyram PlusTek RA843 Nylon 6.6, Impact Modified Impact modified polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Linear Mold Shrinkage | 0.015 - 0.019 cm/cm | 0.015 - 0.019 in/in | |
| Polyram PlusTek RA844 Nylon 6.6, UV Stabilized Impact modified, UV and heat stabilized polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Linear Mold Shrinkage | 0.015 - 0.019 cm/cm | 0.015 - 0.019 in/in | |
| Polyram PlusTek RA846 Nylon 6.6, Impact Modified Impact modified and heat stabilized polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Linear Mold Shrinkage | 0.011 - 0.019 cm/cm @Thickness 3.20 mm |
0.011 - 0.019 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
| A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy DescriptionFormion® FI 241E is a patented non-reinforced, extrusion grade Ionomer alloy. It has bee formulated for high durability, low gloss, and low temperature ductility.ApplicationFormion® FI.. |
|||
| Linear Mold Shrinkage | 0.011 - 0.019 cm/cm @Thickness 3.20 mm |
0.011 - 0.019 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
| A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy DescriptionFormion® FI 241E is a patented non-reinforced, extrusion grade Ionomer alloy. It has bee formulated for high durability, low gloss, and low temperature ductility.ApplicationFormion® FI.. |
|||
| Linear Mold Shrinkage | 0.014 - 0.019 cm/cm | 0.014 - 0.019 in/in | ASTM D955 |
| Clariant Renol 6608-L Nylon 66, High Impact Modified, Lubricated Data provided by Clariant Masterbatches |
|||
| Linear Mold Shrinkage | 0.014 - 0.019 cm/cm | 0.014 - 0.019 in/in | ASTM D955 |
| Clariant Renol 6608-L UV Black Nylon 66, High Impact Modified, Lubricated, UV Stable Data provided by Clariant Masterbatches |
|||