Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 7.0 - 11 g/10 min @Load 5.00 kg, Temperature 200 °C |
7.0 - 11 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
NIZHNEKAMSKNEFTEKHIM 524B General Purpose Polystyrene Polystyrene intended to produce glossy coating by co-extrusion. A specialty recipe provides for drastic reduction of buildup in a die plate and of streaks on an article in molding.Information provi.. |
|||
Melt Flow | 7.0 - 11 g/10 min @Load 5.00 kg, Temperature 200 °C |
7.0 - 11 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
NIZHNEKAMSKNEFTEKHIM 525 General Purpose Polystyrene Grade 525 is a crystal polystyrene for both injection molding and cap layer co-extrusion. Injection molding applications such as medical and laboratory parts, tumblers, and jewel boxes demonstrate t.. |
|||
Melt Flow | 4.0 - 11 g/10 min @Load 1.20 kg, Temperature 300 °C |
4.0 - 11 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Polymer Resources PC-G5-IM Polycarbonate, 5% Glass Reinforced, Impact Modified, Foamable Polycarbonate, 5% Glass Reinforced, Impact Modified, FoamableProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inf.. |
|||
Melt Flow | 9.0 - 11 g/10 min @Load 5.00 kg, Temperature 190 °C |
9.0 - 11 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
FKuR Kunststoff Fibrolon® F 8530 Biodegradable Wood-Plastic Compound, Fiber Reinforced FIBROLON® are fiber reinforced compounds. Depending on specific customer requirements either a biodegradable polymer or a polyolefin can be used as the polymeric matrix. With the brand name of F.. |
|||
Melt Flow | 8.0 - 11 g/10 min | 8.0 - 11 g/10 min | ASTM D1238 |
Kolon KOCETAL® EL306 Toughened Grade Acetal Resin Flexible grade. Applications: Flexible products. Information provided by API-Kolon. |
|||
Melt Flow | 8.5 - 11 g/10 min | 8.5 - 11 g/10 min | ASTM D1238 |
Kolon KOCETAL® GF705 G/F Reinforced Acetal Resin Glass fiber reinforced, improved stiffnessApplications: Products for high stiffness, improved fatigue properties. Information provided by API-Kolon. |
|||
Melt Flow | 8.5 - 11 g/10 min | 8.5 - 11 g/10 min | ASTM D1238 |
Kolon KOCETAL® MS301 Wear Modified Acetal Resin Molybdenum disulfide added, improved wear property. Applications: Products for low noise and friction against metal. Information provided by API-Kolon. |
|||
Melt Flow | 9.0 - 11 g/10 min | 9.0 - 11 g/10 min | 230/2.16 (typical); ASTM D1238 |
Fiberfil® J-68/25/E/SD Polypropylene Copolymer, 25% Glass Fiber Reinforced, Chemically coupled, with static dissipation Information provided by FIBERFIL Engineered Plastics |
|||
Melt Flow | 5.0 - 11 g/10 min | 5.0 - 11 g/10 min | ASTM D1238 - ISO 1133 |
DuPont Elvaloy® 4170 Reactive Ethylene Terpolymer (RET) A reactive ethylene terpolymer (RET) that can be used to modify the properties of asphalt binder used in paving.Elvoy® 4170 is the most chemically reactive of the terpolymers manufactured by DuPont.. |
|||
Melt Flow | 3.0 - 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 - 11 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 3.0 - 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 - 11 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 3.0 - 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 - 11 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 3.0 - 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 - 11 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 3.0 - 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 - 11 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 9.0 - 11 g/10 min @Load 1.20 kg, Temperature 300 °C |
9.0 - 11 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Adell DS-10 General Purpose Polycarbonate |
|||
Melt Flow | 8.0 - 11 g/10 min | 8.0 - 11 g/10 min | |
Ashley Polymers Ashlene® RH190H2-B Acetal General purpose, reprocessed homopolymer, excellent toughness, strength, stiffness and lubricity. UV stabilized with carbon black for outstanding weatherability.Data provided by the manufacturer |
|||
Melt Flow | 8.0 - 11 g/10 min | 8.0 - 11 g/10 min | |
Ashley Polymers Ashlene® RH190 Acetal General purpose, reprocessed homopolymer, excellent toughness, strength, stiffness and lubricity. Available in Natural and Black. Natural: Designated RH190N-3; Black: Designated RH190B.Data provid.. |
|||
Melt Flow | 3.0 - 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 - 11 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 7.0 - 11 g/10 min | 7.0 - 11 g/10 min | ASTM D1238 |
Buckeye Polymers BP RPP 1509 GK BLK Polypropylene, 15% Glass Filled Product Information: 15% glass reinforced polypropyleneProduct Features:Offers improved flex modulus while maintaining a low specific gravity propertyChemically coupled for improvved physical proper.. |