| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Exxon Chemical |
| Trade Name | EXACT™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Exact™ 4151 Ethylene-based Plastomer Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Exact 4151 is an ethylene-based hexane plastomer produced using ExxonMobil Chemical’s EXXPOL® Catalyst Technology. Exact 4151 is designed for both monolayer and multilayer coextrusion cast and blown film applications requiring low sealing temperatures, high oxygen transmission and high toughness. Typical applications include seal layers for lamination films used in meat, poultry and produce packaging. Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoThermal Stabilizer: YesApplications:Blown FilmLamination Film Information provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.895 g/cc | 0.0323 lb/in³ | ExxonMobil method |
| Melt Flow | 2.2 g/10 min | 2.2 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 4.21 MPa | 610 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 4.00 MPa | 580 psi | ASTM D882 |
| Film Elongation at Yield, MD | 10 % | 10 % | ASTM D882 |
| Film Elongation at Yield, TD | 9.0 % | 9.0 % | ASTM D882 |
| Puncture Energy | 7.57 J | 5.58 ft-lb | ExxonMobil Method |
| Elmendorf Tear Strength MD | 220 g | 220 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 340 g | 340 g | ASTM D1922 |
| Dart Drop Test | 1200 g | 2.65 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 75.8 MPa | 11000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 68.9 MPa | 10000 psi | ASTM D882 |
| 1% Secant Modulus, MD | 55.8 MPa | 8100 psi | ASTM D882 |
| 1% Secant Modulus, TD | 60.7 MPa | 8800 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | <= 190 °C | <= 374 °F | Peak Melting Point; ExxonMobil method |
| Crystallization Temperature | <= 160 °C | <= 320 °F | Peak; ExxonMobil Method |
| Vicat Softening Point | 76.1 °C | 169 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 5.1 % | 5.1 % | ASTM D1003 |
| Gloss | 70 % | 70 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Puncture Force | 16 lbf | ExxonMobil Method |