Physical Properties | Metric | English | Comments |
---|---|---|---|
ESCR 100% Igepal® | 4.0 hour @Thickness 3.80 mm, Temperature 50.0 °C |
4.0 hour @Thickness 0.150 in, Temperature 122 °F |
non slit; ASTM D1693 |
Lotte Chemical Titan TITANEX® LI5011 Linear low density polyethylene resin
(discontinued **) LI5011 is a pelleted high flow linear low density polyethylene. The higher melting point of the resin allows for higher end-use temperatures.Applications: House-wares, toys, lids, containers.Advan.. |
|||
ESCR 100% Igepal® | <= 4.0 hour @Temperature 50.0 °C |
<= 4.0 hour @Temperature 122 °F |
h/F50; Compression molded 2mm notched-plaques; ASTM D1693 |
Braskem Green PE SHA7260 Injection Molding High Density Polyethylene Description: SHA7260 is a high-density polyethylene, developed for the injection molding, easy to process and with high productivity. This resin has a good melt flow with high rigidity and hardness... |
|||
ESCR 100% Igepal® | <= 4.0 hour @Thickness 2.00 mm, Temperature 50.0 °C |
<= 4.0 hour @Thickness 0.0787 in, Temperature 122 °F |
0.3 mm notched-plaques; ASTM-D1693 |
Braskem HC7260LS-L HDPE Injection Molding Polyethylene HC7260LS-L is a high-density polyethylene developed for injection molding. It has high hardness and stiffness and low warpage. This resin also has additives against ultraviolet radiation action. Its.. |
|||
ESCR 100% Igepal® | <= 4.0 hour @Thickness 2.00 mm, Temperature 50.0 °C |
<= 4.0 hour @Thickness 0.0787 in, Temperature 122 °F |
0.3 mm notched-plaques; ASTM-D1693 |
Braskem HA7260 HDPE Injection Molding Polyethylene HA7260 is a high-density polyethylene that was developed for injection molding. It is easy to process and has high productivity, high rigidity and hardness, and a good melt flow. Its narrow molar ma.. |
|||
ESCR 100% Igepal® | <= 4.0 hour @Temperature 50.0 °C |
<= 4.0 hour @Temperature 122 °F |
h/F50; Compression molded 2mm notched-plaques; ASTM D1693 |
Braskem Green PE SHC7260 Injection Molding High Density Polyethylene Description: SHC7260 is a high-density polyethylene, developed for the injection molding which presents high hardness and stiffness, besides low tendency to warpage. The minimum biobased content of .. |