Polymer Property : Modulus of Elasticity = 12.0 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	12.0 GPa	1740 ksi	ASTM D638
Owens Corning Glass Fiber Reinforced Polyester SMC (Compression), 20 wt.% glass Polyester thermosets are available in many formulations. They can be formulated for good to excellent resistance to acids, weak alkalis, and organic solvents. However, they are not recommended for u..
Modulus of Elasticity	12.0 - 14.0 GPa	1740 - 2030 ksi	Compression; ISO 527
Raschig Group 4552 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to +/- 300°C continuously, excellent electrical properties, good mechanical strength, very good dimensional stabi..
Modulus of Elasticity	12.0 - 32.0 GPa @Temperature 60.0 - 150 °C	1740 - 4640 ksi @Temperature 140 - 302 °F	Average value: 22.8 GPa Grade Count:1
Overview of materials for Polyphthalamide (PPA), Carbon Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Carbon Fiber". Each property range of values reported is minimum and maximum values of ..
Modulus of Elasticity	12.0 - 24.5 GPa	1740 - 3550 ksi	Average value: 18.5 GPa Grade Count:13
Overview of materials for Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled". Specific grades with glass content between 45% an..
Modulus of Elasticity	12.0 GPa	1740 ksi
Lehmann & Voss LUVOCOMÂ® 1105-7185 PEEK, with carbon fiber, PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; low thermal coefficient of expansion.Dynamic stressed parts at high m..
Modulus of Elasticity	12.0 GPa	1740 ksi
Lehmann & Voss LUVOCOMÂ® 1105-8422 PEEK, with carbon fiber, PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; low thermal coefficient of expansion.Dynamic stressed parts at high m..
Modulus of Elasticity	12.0 GPa	1740 ksi
Lehmann & Voss LUVOCOMÂ® 1301-7508 PPS, linear, with glass spheres Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.Strong, stiff parts.High continuous use and heat distortion temperature. Non flammable.High chemic..
Modulus of Elasticity	12.0 GPa	1740 ksi
Lehmann & Voss LUVOCOMÂ® 1-7332/GY Polyamide 66, with carbon fiber and PTFE, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Improved friction and wear beh..
Modulus of Elasticity	12.0 GPa	1740 ksi
Lehmann & Voss LUVOCOMÂ® 1850/CF/15/TF/10/EM PBT, with carbon fiber, PTFE, easy flowing Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Electrically conductive, suita..
Modulus of Elasticity	12.0 GPa	1740 ksi
Lehmann & Voss LUVOCOMÂ® 20-0778 Polyphthalamide, with glass fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Low influence from moisture an..
Modulus of Elasticity	12.0 GPa	1740 ksi
Lehmann & Voss LUVOCOMÂ® 20-0778/BK Polyphthalamide, with glass fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Low influence from moisture an..
Modulus of Elasticity	12.0 GPa	1740 ksi
Lehmann & Voss LUVOCOMÂ® 20-8244 Polyphthalamide, with carbon fiber and glass fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Electrically conductive..
Modulus of Elasticity	12.0 GPa	1740 ksi
Lehmann & Voss LUVOCOMÂ® 20-8261 Polyphthalamide, with carbon fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Dynamic stressed parts at high movement velocity.Improved friction and wear..
Modulus of Elasticity	12.0 GPa	1740 ksi
Lehmann & Voss LUVOCOMÂ® 3-8437 Polyamide 6, with glass fiber Applications: Automotive industry, textile machinery, apparatus- and precision engineering.High-strength and stiff parts with low creep.Emergency running property.Suitable for metall inserts.Control..
Modulus of Elasticity	12.0 GPa	1740 ksi	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 0170 Unsaturated Polyester UP SMC 0170 is a general purpose SMC for applications in the field of electrical industry. Typical applications are housings, covers, wire distribution boxes and metering cabinets. The material meets t..
Modulus of Elasticity	12.0 GPa	1740 ksi	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 0390 Unsaturated Polyester UP SMC 0390 is a standard low profile SMC. Because of its low shrinkage, the material shows good surface quality as well as very low warpage. The product is suitable for applications if a better surfac..
Modulus of Elasticity	12.0 GPa	1740 ksi	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 1500 Unsaturated Polyester UP SMC 1500 is a special SMC for applications calling for high continuous service temperature. The glass level has been selected to combine good mouldability with good strength and stiffness properties..
Modulus of Elasticity	12.0 GPa	1740 ksi	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 2600 Unsaturated Polyester UP SMC 2600 is a special SMC with electrically conductive properties. Because of its conductivity, SMC 2600 is antistatic and prevents build-up of electrical charges on the surface. Despite of its cond..
Modulus of Elasticity	12.0 GPa	1740 ksi
Lehmann & Voss LUVOCOMÂ® 1/CF/15/HS Polyamide 66, with carbon fiber, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia comp..
Modulus of Elasticity	12.0 GPa	1740 ksi	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 0150 Unsaturated Polyester UP SMC 0150 is a general purpose SMC for applications in the field of electrical industry. Typical applications are housings, covers, wire distribution boxes and metering cabinets. The material meets t..
Modulus of Elasticity	12.0 GPa	1740 ksi	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 0160 Unsaturated Polyester UP SMC 0160 is a general purpose SMC for applications in the field of electrical industry. Typical applications are housings, covers, wire distribution boxes and metering cabinets. The material meets ..
Modulus of Elasticity	12.0 GPa	1740 ksi	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 0290 Unsaturated Polyester UP SMC 0290 is a specially formulated SMC processable by injection moulding. The gentle production process prevents the fiber from any damage. Parts made of SMC 0290 reach higher levels of strength and..
Modulus of Elasticity	12.0 GPa	1740 ksi	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 0300 Unsaturated Polyester UP SMC 0300 is a low shrink standard SMC providing improved surface quality, reduced shrinkage and warpage. Typical fields of applications are mechanical engineering and electrical industry, where impr..
Modulus of Elasticity	12.0 GPa	1740 ksi	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 1800 Unsaturated Polyester UP SMC 1800 is for structural applications requiring extreme high mechanical properties and low weight. These compounds mould to parts focussing on mechanical strength for replacement of metals in ord..
Modulus of Elasticity	12.0 GPa	1740 ksi
Lehmann & Voss LUVOCOMÂ® 1100/GF/30/NAT Polyether sulfone, with glass fiber Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.High dimensionally sta..
Modulus of Elasticity	12.0 GPa	1740 ksi	ISO 527-1/-2
BASF Ultramid® KR 4355 G7 35% Glass Filled PA6/6T (Conditioned) Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r..
Modulus of Elasticity	12.0 GPa @Temperature 0.000 °C	1740 ksi @Temperature 32.0 °F	ISO 527
BASF Ultramid® KR 4355 G7 35% Glass Filled PA6/6T (Dry) Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r..
Modulus of Elasticity	12.0 GPa @Temperature 40.0 °C	1740 ksi @Temperature 104 °F	ISO 527
BASF Ultramid® KR 4355 G7 35% Glass Filled PA6/6T (Dry) Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r..