Polymer Property : Flexural Strength = 200 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	200 MPa	29000 psi
Plastcom SLOVASTER® B/E GF 30 PBT, 30% glass fibre FeaturesPBT/PET for injection moulding, chemically reinforced with 30% glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and ben..
Flexural Strength	200 MPa	29000 psi	10mm/min; DIN 53452
Qualchem Danamid FGF-15 Polyamide 6, 15% Glass Fiber Reinforced with glass fiber.Information provided by Qualchem Zrt.
Flexural Strength	200 MPa	29000 psi	ISO 178
Nilit FRIANYL B63 H-GV25 Nylon 6 for injection molding, 25% glass fiber reinforced Nylon 6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength	200 MPa	29000 psi
Lehmann & Voss LUVOCOMÂ® TPI-0953 Thermoplastic polyimide, with carbon fiber, PTFE, lubricant modified Applications: Automotive industry, textile machinery, apparatus- and precision engineering medical- and electrical enineering, aircraft- and aerospace industry.Very high continuous use and heat dist..
Flexural Strength	200 MPa	29000 psi	ISO 178
Grupo Repol DinalonÂ® B1X25 G30V0 PA6 30% Glass Fiber, V0 Red Phosphorus and Halogen Free Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
Flexural Strength	200 MPa	29000 psi	ISO 178
Solvay TECHNYLÂ® A 30 H1 V30 PA66, 30% glass fiber, DRY Description: TECHNYLÂ® A 30H1 V30 is a brominated flame retardant polyamide 66, reinforced with 30% of glass fiber, for injection molding. This product is available in natural & black color.Benefi..
Flexural Strength	200 MPa	29000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON AE008XXY ABS LNP* STAT-KON* AE008XXY is a compound based on ABS resin containing 40% Carbon Fiber. Added feature of this material ia: Electrically Conductive.
Flexural Strength	200 MPa	29000 psi	ISO 178
SABIC Innovative Plastics LNP Stat-kon DEL339XC PC LNP STAT-KON* DEL339XC is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supp..
Flexural Strength	200 - 350 MPa	29000 - 50800 psi
Sinotek Materials CFC Carbon Heat Insulation Material Information provided by Sinotek
Flexural Strength	200 MPa	29000 psi	ISO 178
Solvay TECHNYLÂ® AR 218 V25 Nylon 66, 25% glass fiber, DRY Description: Polyamide PA66 reinforced with 25% of glass fiber, heat stabilized, containing recycled material.Available in: Europe and North AmericaProduct Applications: TECHNYLÂ® AR 218 V25 BLACK..
Flexural Strength	200 MPa	29000 psi	ASTM D790
Techmer ES HiFillÂ® PET GF/M40 BK 40% Glass/Mineral Fiber Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral, 40% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc.
Flexural Strength	200 MPa	29000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP PF004 PA 6 (Europe-Africa-Middle East) 20% glass fibre reinforced Polyamide 6 injection moulding resin.
Flexural Strength	200 MPa	29000 psi	ASTM D790
Chase Plastics CP Pryme® N120GL (DAM) Nylon 6, 20% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics.
Flexural Strength	200 MPa	29000 psi	ASTM D790
Chase Plastics CP Pryme® NN133TL (Dry) Nylon 66, 33% Glass Fiber Reinforced, Lubricated, Impact Modified Features: Impact modifiedLubricatedGood toughnessForm: PelletsInformation provided by Chase Plastics.
Flexural Strength	200 MPa	29000 psi	At Rupture; ISO 178
Vyncolit X7010 Novolac Phenolic Glass fiber reinforced molding compound with excellent mechanical and thermal properties.USES: Information provided by Vyncolit, a Sumitomo Bak Group
Flexural Strength	200 MPa	29000 psi	ASTM D790
Polyram PlusTek RA325G5 Nylon 6.6, 25% Glass Fiber, Flame Retardant 25% glass fiber reinforced, self extinguishing halogen free polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	200 MPa	29000 psi	ASTM D790
Polyram PlusTek RB306G6 Nylon 6, 30% Glass Fiber 30% glass-fiber reinforced. Heat stabilized polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	200 MPa	29000 psi	ISO 178
DuPont Performance Polymers Crastin® SK605 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**) 30% Glass Reinforced Polybutylene Terephthalate Crastin SK605 NC010 is a 30% glass fiber reinforced lubricated polybutylene terephthalate resin for injection molding.Information provided by DuPont P..
Flexural Strength	200 MPa	29000 psi	ASTM D790
Aclo Accutech Polycarbonate POL051G30L Glass Reinforced
Flexural Strength	200 MPa	29000 psi	ASTM Test
BASF Ultramid® SEGM35 H1 BK-126 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid SEGM35 H1 BK-126 is a 40% glass/mineral reinforced injection molding grade. It offers enhanced surface appearance, it also exhibits similar UV weathering characteristics compared to 8267G ..
Flexural Strength	200 MPa	29000 psi	ASTM D790
Beijing Chemical Industry KAIFA® MN301-G25 Nylon 66 Resin 25% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group)
Flexural Strength	200 MPa	29000 psi	ISO 178
BASF Ultradur® B 4300 G6 LT 30% Glass Filled BK 150926 PBT Description: Easy flowing injection molding grade with 30 % glass fibers; for rigid, tough and dimensionally stable technical parts (eg windshield wiper arms, printed circuit boards PCBs), housing, ..