Polymer Property : Compressive Modulus = 2.28 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Modulus	2.28 GPa	330 ksi	ASTM D695
Quadrant EPP Nylatron® LFG (ASTM Product Data Sheet)
Compressive Modulus	2.28 GPa	330 ksi	ASTM D695
Quadrant EPP Nylatron® LIG Oil Filled Cast 6 Nylon (ASTM Product Data Sheet)
Compressive Modulus	2.28 - 124 GPa	330 - 18000 ksi	Average value: 29.6 GPa Grade Count:14
Overview of materials for Polyetheretherketone, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Carbon Fiber Filled". Each property range of values reported is minimum and maximu..
Compressive Modulus	2.28 - 5.45 GPa	330 - 791 ksi	Average value: 3.21 GPa Grade Count:5
Overview of materials for Polyetheretherketone, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, PTFE Filled". Each property range of values reported is minimum and maximum values..
Compressive Modulus	2.28 - 3.00 GPa	330 - 435 ksi	Average value: 2.63 GPa Grade Count:4
Overview of materials for Nylon 6, Glass Fiber/Solid Lube Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass Fiber/Solid Lube Filled". Each property range of values reported is minimum and maximum v..
Compressive Modulus	2.28 GPa	330 ksi	ASTM D695
Ensinger Tecapeek® XP-100 Compression Molded PEEK Compound, Bearing Grade Material with 10% Graphite, 10% PTFE, and 10% Carbon Fiber Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in..
Compressive Modulus	2.28 GPa	330 ksi
Abatron AboCast 8103-11 One Part Epoxy One component system. Information provided by Abatron, Inc.Processing: Shelf life 6-8 months at 25°C (77°F). Heat cured; Pot life 190 min. at 100°C (212°C). Peak exotherm 170°C (340°F). At..