Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Modulus | 2.28 GPa | 330 ksi | ASTM D695 |
Quadrant EPP Nylatron® LFG (ASTM Product Data Sheet) |
|||
Compressive Modulus | 2.28 GPa | 330 ksi | ASTM D695 |
Quadrant EPP Nylatron® LIG Oil Filled Cast 6 Nylon (ASTM Product Data Sheet) |
|||
Compressive Modulus | 2.28 - 124 GPa | 330 - 18000 ksi | Average value: 29.6 GPa Grade Count:14 |
Overview of materials for Polyetheretherketone, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Carbon Fiber Filled". Each property range of values reported is minimum and maximu.. |
|||
Compressive Modulus | 2.28 - 5.45 GPa | 330 - 791 ksi | Average value: 3.21 GPa Grade Count:5 |
Overview of materials for Polyetheretherketone, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, PTFE Filled". Each property range of values reported is minimum and maximum values.. |
|||
Compressive Modulus | 2.28 - 3.00 GPa | 330 - 435 ksi | Average value: 2.63 GPa Grade Count:4 |
Overview of materials for Nylon 6, Glass Fiber/Solid Lube Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass Fiber/Solid Lube Filled". Each property range of values reported is minimum and maximum v.. |
|||
Compressive Modulus | 2.28 GPa | 330 ksi | ASTM D695 |
Ensinger Tecapeek® XP-100 Compression Molded PEEK Compound, Bearing Grade Material with 10% Graphite, 10% PTFE, and 10% Carbon Fiber Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in.. |
|||
Compressive Modulus | 2.28 GPa | 330 ksi | |
Abatron AboCast 8103-11 One Part Epoxy One component system. Information provided by Abatron, Inc.Processing: Shelf life 6-8 months at 25°C (77°F). Heat cured; Pot life 190 min. at 100°C (212°C). Peak exotherm 170°C (340°F). At.. |