Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 22.0 MPa | 3190 psi | ASTM D 638 |
Polyplastic Torlen® PE 2K 901 High Density Polyethylene, Carbon Filled Information provided by PolyPlastic Group. |
|||
Tensile Strength at Break | 22.0 - 38.0 MPa | 3190 - 5510 psi | ASTM D638 |
Proto3000 Accura® Amethyst™ Material for use with Viper™ SLA® systems Optimized for the rapid and automated production of patterns and master molds for jewelry manufacturing. FEATURES:Outstanding accuracyExceptional detailHigh thermal resistanceDeep purple colorLow as.. |
|||
Tensile Strength at Break | <= 22.0 MPa | <= 3190 psi | ISO/R527 |
Polykemi AB POLYfill PP EIP5025 F VT2 Polypropylene, Mineral Reinforced, Extrusion grade, Low CLTE Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 22.0 MPa | <= 3190 psi | ISO/R527 |
Polykemi AB POLYfill PPHC K2040H Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 50 mm/min test speed; ASTM D 638 |
NOVA Chemicals Sclair® IG454-A Compression Molded HDPE Resin IG454-A complies with the U.S. FDA specifications for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food. IG454.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | ISO 527 |
SABIC Innovative Plastics LNP KONDUIT MT00E PP LNP KONDUIT* MT00E is a compound based on Polypropylene resin containing 70% Proprietary Thermal Filler. Added features of this material include: Thermally Conductive. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | |
Plastcom SLOVALEN PC 93 T 20 PP, 20% mineral filling, UV stabilization FeaturesModified PP for injection moulding with the content of 20 % mineral filling, uv stabilized. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased.. |
|||
Tensile Strength at Break | <= 22.0 MPa | <= 3190 psi | ISO/R527 |
Polykemi AB POLYfill PP HJ752 UV Polypropylene/Elastomer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 22.0 MPa | <= 3190 psi | ISO/R527 |
Polykemi AB POLYfill PPH K20040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | ISO 527 |
FKuR Kunststoff Fibrolon® P 7550 Wood-Plastic Compound, Fiber Reinforced FIBROLON® are fiber reinforced compounds. Fibrolon® P 7550 has a polypropylene base. With the brand name of FIBROLON® FKuR has developed natural fiber reinforced compounds (Wood-Plastics-C.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | |
JPJ Technologies 7600M HDPE Extrusion Information provided by JPJ Technologies |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL WCA901 PPE-TPE Non-Halogenated flame retardant, flexible Noryl resin intended for evaluation in wire and cable applications, capable of meeting VW-1 and 105°C end use temperature requirements as defined by UL.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Lubricomp ML002S PP LNP* Lubricomp* ML002S is a compound based on Polypropylene containing PTFE. Characteristics of this grade are: Heat Stabilized and Internally Lubricated.This data was supplied by SABIC-IP for the.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP ML004LS PP LNP* LUBRICOMP* ML004LS is a compound based on Polypropylene resin containing 20% PTFE. Added features of this matLNP* Lubricomp* ML004LS is a compound based on Polypropylene resin containing PTFE... |
|||
Tensile Strength at Break | >= 22.0 MPa | >= 3190 psi | ASTM D638 |
Solvay Specialty Polymers Hyflon® PFA P455 Perfluoroalkoxy (PFA) Hyflon® PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat res.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP 2Z004 ETFE LNP* THERMOCOMP* 2Z004 is a compound based on ETFE resin containing 20% Milled Glass. |
|||
Tensile Strength at Break | >= 22.0 MPa | >= 3190 psi | |
Sibur SKS-30 ARKM-27 1st Group Oil-Filled Styrene-Butadiene Rubber SBR 1712. For use in the tire industry for production of tire thread and other parts for tires, in the rubber technical industry for production of a wide assortment of rubber technical articles, an.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | ASTM D638 |
SCG Chemicals EL-Proâ„¢ P750J Polypropylene Injection Molding Key Characteristics:Excellent clarityHigh productivityGood processability and stiffnessHigh glossOdorlessSafe for food contactRecommended Applications:Food container, utensilMedical parts such as sy.. |
|||
Tensile Strength at Break | >= 22.0 MPa | >= 3190 psi | 25mm/min; ISO 527 |
Borealis Supersmooth™ LE0592S Polyethylene Supersmooth™ LE0592S is a crosslinkable black polyethylene compound, specially designed for bonded semiconductive screen applications. Supersmooth™ LE0592S is intended for semiconductive applicat.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | ISO 527-2 |
Total PS CPDS 9217 Compound Polystyrene/Polyethylene POLYSTYRENE (PS) COMPOUND (CPDS) 9217 is an alloy of polystyrene and polyethylene. This combination brings the benefits of polyethylene; a high level of stress crack resistance, mechanical properti.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | |
Daikin DAI-EL G-801 Fluoroelastomer Copolymer, Peroxide Curable Grade, 66% Fluorine Content Offers excellent chemical and steam resistance. Offers good mechanical characteristics.Features: Good low-temperature and elasticity characteristics.Information provided by Daikin Industries. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | |
Daikin DAI-EL G-901 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 71% Fluorine Content Offers excellent chemical and steam resistance. Offers good mechanical characteristics.Features: Excellent solvent resistance.Information provided by Daikin Industries. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 50 mm/min; ISO 527 |
Chi Mei Polyrex® PH-88 Polystyrene - High Impact High impact |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | ISO 527-1/-2 |
DuPont Performance Polymers Hytrel® PC948 NC010 Polyester Elastomer TPC-ET
(Unverified Data**) 40 Shore D High Performance Polyester Elastomer Developed for the Healthcare Industry Hytrel SC948 NC010 is a low modulus grade with nom. durometer hardness of 40D contains non-discoloring stabilize.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | ISO R 527 |
Fainplast Compounds PM 99 Flexible PVC, Extrusion Semi-rigid for handrail |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 50mm/min; ASTM D638 |
3M Dyneon™ PVDF 31508/0003 Polyvinylidene Fluoride 3M™ Dyneon™ PVDF 31508/0003 is a flexible copolymer of VF2 and CTFE, exhibiting very low shrinkage and excellent impact resistance. PVDF 31508/0003 also has a very low brittleness temperature, for.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 50mm/min; ASTM D638 |
3M Dyneon™ PVDF 31508/0009 Polyvinylidene Fluoride 3M™ Dyneon™ PVDF 31508/0009 is a flexible copolymer of VF2 and CTFE, exhibiting very low shrinkage and excellent impact resistance. Dyneon PVDF 31508/0009 also has a very low brittleness temperatu.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | ASTM D638 |
UBE V106 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 50mm/min; ASTM D638 |
3M Dyneon™ PVDF 32008/0000 Polyvinylidene Fluoride
(discontinued **) Copolymer of VF2 and CTFEUltra-flexibleVery low shrinkage ratesWide operating temperature windowProcessable using a variety of thermoplastic conversion techniquesInformation provided by Dyneon, A 3M.. |