Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 22.1 MPa | 3200 psi | 2 in/min; ASTM D638 |
RheTech Products CS30P100-01UV 30% Ceramic Sphere Reinforced Polypropylene, UV Stabilized, Black Applications: Consumer goodsHousingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | 2 in/min; ASTM D638 |
RheTech Products P249-01UV General Purpose Polypropylene Copolymer, UV Stabilized, Black Applications: LP bracketsSplash shieldsDoor/trunk scuffInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | 2 in/min; ASTM D638 |
RheTech Products P601-01 Polypropylene Copolymer, Black Applications: Engine componentChassis componentConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | 2 in/min; ASTM D638 |
RheTech Products RCC220-01 20% Calcium Carbonate Reinforced Polypropylene Copolymer, Black, Recycled Content Applications: I/P hush panelsSplash shieldsUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | ASTM D638 - ISO 527-2 |
DuPont Bexloy® AXW504BK Modified Ionomer Resin
(discontinued **) A modified ionomer resin engineered for injection molded exterior automotive applications.Availability: North AmericaInformation provided by DuPont. |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | ASTM D4745 |
3M Dyneon™ CC155 Custom Fluoropolymer Compound
(discontinued **) This compound consists of a mixture of 50% stainless steel blended with PTFE.Information provided by Dyneon, A 3M Company |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | ASTM D638 |
LyondellBasell Alathon® ETP H4837 High Density Polyethylene ApplicationsALATHON H 4837 is a high-flow “freezer†grade resin that exhibits enhanced cold temperature impact performance, enhanced processability and thermal stability, with good color a.. |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | ASTM D638 |
Spartech Formalloy LG Low-Gloss TPO Alloy Specialty Sheet Description: Specialty SheetInformation provided by Spartech. |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | ASTM D638 |
Teknor Apex APEX® 590 Polyvinyl Chloride, Flexible Notes: RoHS Compliant Features: General Purpose Uses: Tubing; Wire Jacketing Agency Ratings: UL 498; UL 62 Wire Types: SPT-1; SPT-2 Processing Method: Injection MoldingForms: PelletsInformation Prov.. |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | ASTM D638 |
Teknor Apex APEX® 65002 Polyvinyl Chloride, Flexible Notes: 105°C Jacket; RoHS Compliant Features: Flame Retardant; Lead-free Uses: Communication Wire JacketingForms: Pellets Agency Ratings: NEC Article 725; NEC Article 760; NEC Article 770; NEC Ar.. |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | ASTM D638 |
Teknor Apex APEX® 80851 Polyvinyl Chloride, Flexible Notes: 105°C Insulation; RoHS Compliant Forms: Pellets Uses: Insulation; Wire and Cable Applications Wire Types: AWM; THW; TW; THHN; THWN Agency Ratings: MIL W-16878; UL QMTT2 .E73402Information .. |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | ASTM D638 |
Teknor Apex APEX® 80851-F Polyvinyl Chloride, Flexible Notes: 105°C Insulation; RoHS Compliant Forms: Pellets Uses Wire and Cable ApplicationsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | ASTM D638 |
Teknor Apex APEX® 82_E254V-14 Polyvinyl Chloride, Flexible Notes: 80°C Jacket; RoHS CompliantForms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | ASTM D412 |
Teknor Apex MF 826 Polyvinyl Chloride, Flexible Film Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Film, Medical Applications Forms-PelletsInformation provided by Teknor Apex Company |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | ASTM D638 |
Teknor Apex APEX® 02-A0111A-90NT Polyvinyl Chloride, Flexible Notes: RoHS Compliant Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 22.1 MPa | 3210 psi | ASTM D638 |
DuPont Surlyn® 8945 Thermoplastic Ionomer Resin Surlyn® 8945 provides high flow properties and consistent, easy processing in molded and extruded applications. It is positioned in the medium/high acid, high neutralization area of the ionomer sp.. |
|||
Tensile Strength at Break | 22.1 MPa | 3210 psi | 500mm/min; ASTM D638 |
Westlake MC3016 High Density Polyethylene Coating Westlake MC3016 is a high density polyethylene designed for extrusion coating and lamination applications. MC3016 provides improved barrier properties, temperature resistance, stress crack resistanc.. |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow DOWLEX™ IP-51 High Density Polyethylene Resin (HDPE) DOWLEX™ IP-51 is an Improved Processing high density resin designed to offer excellent process-ability and impact performance. This resin was designed by optimization of the breadth, shape and pea.. |
|||
Tensile Strength at Break | 22.1 MPa | 3210 psi | ASTM D882 |
3M Scotch-Weld™ DP805 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP805 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability .. |
|||
Tensile Strength at Break | 22.1 MPa | 3210 psi | ASTM D638 Die C |
3M Scotch-Weld™ TE230 Black Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as .. |
|||
Tensile Strength at Break | 22.1 MPa | 3210 psi | |
Asahi Glass Fluon® PA1020Z 20% Glass Fiber, PTFE Filled Compound Fluon®PTFE FC has improved creep and wear resistance. A wide range of fillers such as glass fiber, graphite, bronze, carbon fiber are available. Information provided by Asahi Glass Company, Inc. |
|||
Tensile Strength at Break | 22.1 MPa | 3210 psi | ASTM D638 Die C |
3M Scotch-Weld™ TS115 HGS Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as .. |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | ASTM D638 - ISO 527-2 |
DuPont Bexloy® AXW502NC010 Modified Ionomer Resin
(discontinued **) A modified ionomer resin engineered for injection molded exterior automotive applications.Availability: North AmericaInformation provided by DuPont. |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | ASTM D638 - ISO 527-2 |
DuPont Bexloy® AXW604BK 3% Glass Reinforced, Heat Stabilized Modified Ionomer Resin
(discontinued **) A 3% glass reinforced, heat stabilized modified ionomer resin engineered for injection molded interior automotive applications.Availability: North AmericaInformation provided by DuPont. |
|||
Tensile Strength at Break | 22.1 MPa | 3200 psi | 2 in/min; ASTM D638 |
RheTech Products HP508-01UV 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Black Applications: Interior trim, Close out panelsConsolesInjection molding conditions reported in table.Information provided by RheTech Products. |