3M Scotch-Weld™ TE230 Black Polyurethane Reactive Adhesive

Category Polymer , Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ TE230 Black Polyurethane Reactive Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as wood, fiber reinforced plastic (FRP) and many other plastics to themselves, to metal and glass. Sprayable/extrudable grade adhesive with long set time ideal for bonding a wide variety of plastics including polystyrene and polyacrylic. Bonds aluminum and glass to plastic and wood.Information provided by 3M
Physical Properties Metric English Comments
Density >= 1.09 g/cc
>= 0.0394 lb/in³
Brookfield Viscosity 84000 cP
84000 cP
Thermosel using spindle #27
Mechanical Properties Metric English Comments
Hardness, Shore D 42
42
Tensile Strength at Break 22.1 MPa
3210 psi
ASTM D638 Die C
Elongation at Break 825 %
825 %
ASTM D638 Die C
Tensile Modulus 0.0207 GPa
3.00 ksi
ASMT D638 Die C
Shear Strength 1.27 MPa

@Temperature 23.0 °C
184 psi

@Temperature 73.4 °F
Overlap, Polycarbonate
3.10 MPa

@Temperature 82.0 °C
450 psi

@Temperature 180 °F
Overlap, Maple
4.76 MPa

@Temperature 23.0 °C
690 psi

@Temperature 73.4 °F
Overlap, Polystyrene, Substrate Failure
4.83 MPa

@Temperature 82.0 °C
700 psi

@Temperature 180 °F
Overlap, FRP
9.24 MPa

@Temperature 23.0 °C
1340 psi

@Temperature 73.4 °F
Overlap, Polyacrylic, Substrate Failure
9.65 MPa

@Temperature 23.0 °C
1400 psi

@Temperature 73.4 °F
Overlap, ABS, Substrate Failure
10.3 MPa

@Temperature 23.0 °C
1500 psi

@Temperature 73.4 °F
Overlap, Maple
14.5 MPa

@Temperature 23.0 °C
2110 psi

@Temperature 73.4 °F
Overlap, PVC, Substrate Failure
21.4 MPa

@Temperature 23.0 °C
3100 psi

@Temperature 73.4 °F
Overlap, FRP
Peel Strength 7.89 kN/m
45.0 pli
180°, Polystyrene
7.89 kN/m
45.0 pli
180°, Glass
8.24 kN/m
47.0 pli
180°, Polyacrylic
8.24 kN/m
47.0 pli
180°, ABS
8.41 kN/m
48.0 pli
180°, Aluminum
13.7 kN/m
78.0 pli
180°, FRP, Cotton duck failed during testing
15.8 kN/m
90.0 pli
180°, PVC, Cotton duck failed during testing
17.7 kN/m
101 pli
180°, Polycarbonate, Cotton duck failed during testing
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Processing Properties Metric English Comments
Cure Time 2.50 min
0.0417 hour
Set Time
Descriptive Properties Value Comments
Appearance Black