Polymer Property : Tensile Strength at Break = 27600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 190 MPa
27600 psi
STN EN ISO 527-2
Plastcom SLOVAMID 66 GF 35 TS Polyamide 66, 35% Glass Fiber, Thermal Stabilization
FeaturesPA 66 for injection moulding, chemically reinforced with 35% glass fiber, heat stabilized, suitable for high strength and high impact mouldings. Used in the automotive, engineering and elec..
Tensile Strength at Break 190 MPa
27600 psi
ISO 527
Solvay Specialty Polymers Ixef® 3006/9019 Polyarylamide, 30% Carbon Fiber, at Equilibrium (65% RH)  (discontin
The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manufacturer, Solvay A..
Tensile Strength at Break 190 MPa
27600 psi
ISO 527-1/-2
Lanxess Durethan® AKV 30 GIT H2.0 900116 Nylon 66, 30% Glass Fiber
PA 66, injection molding grade, 30% glass fibers, suitable for GIT (gas assisted technology), good surface finish, good heat-ageing resistance
Tensile Strength at Break 190 MPa
27600 psi
ISO 527-1/-2
Lanxess Durethan® BKV 35 H2.0 EF 901510 Nylon 6, 35% Glass Fiber
PA 6, injection molding grade, 35% glass fibers, good heat-ageing resistance, good flowability (easy flow)
Tensile Strength at Break 190 MPa
27600 psi
LATI Latiohm 57-05 PD01 G/15 PPA, 15% Glass Fiber Reinforced
Semiconductive/dissipative product based on Semi-aromatic polyamide (PPA). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by..
Tensile Strength at Break 190 MPa
27600 psi
ISO 527 Type 1A
Solvay TECHNYL® A 218 V30 BK 34 NG PA66, 30% glass fiber, DRY
Description: TECHNYL® A 218 V30 Black 34 NG is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding. The product is available in black color.Benefits: This p..
Tensile Strength at Break 190 MPa
27600 psi
ISO 527 Type 1A
Solvay TECHNYL® C 216 V45 PA6, 45% glass fiber, DRY
Description: Polyamide PA6, reinforced with 45% of glass fiber, for injection molding.Available in: EuropeProduct Applications: TECHNYL C 216 V45 has been optimized to have high impact strength, a n..
Tensile Strength at Break 190 MPa
27600 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP UFL36AS PPA (Europe-Africa-Middle East)
LNP* LUBRICOMP* UFL36AS is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE. Added features include Internally Lubricated, Heat Stabilized.
Tensile Strength at Break 190 MPa
27600 psi
SGL Carbon Group PANOX® FA C063 SSC High performance Crimped staple oxidized textile fiber, For felts and non-wovens
PANOX® is the industry standard when it comes to fire-retardant textile fibers. As an oxidized, thermally stabilized polyacrylonitrile (PAN) fiber that will not burn, melt, soften or drip, PANOX ..
Tensile Strength at Break 190 MPa
27600 psi
SGL Carbon Group PANOX® SA C063 SSC High performance oxidized textile fiber, Crimped staple fiber, For felts and non-wovens
PANOX® is the industry standard when it comes to fire-retardant textile fibers. As an oxidized, thermally stabilized polyacrylonitrile (PAN) fiber that will not burn, melt, soften or drip, PANOX ..
Tensile Strength at Break 190 MPa
27600 psi
SGL Carbon Group PANOX® SA T320 EEA High performance oxidized textile fiber, Continuous Tow with 320k filaments
For carbon/carbon and spinning. PANOX® is the industry standard when it comes to fire-retardant textile fibers. As an oxidized, thermally stabilized polyacrylonitrile (PAN) fiber that will not b..
Tensile Strength at Break 190 MPa
27600 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Stat-kon EE008E PEI
LNP STAT-KON* EE008E is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas r..
Tensile Strength at Break 190 MPa
27600 psi
ISO 527
SABIC Innovative Plastics LNP Verton OV00A PPS (Asia Pacific)
LNP* Verton* OV00A is a compound based on Polyphenylene Sulfide resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break 190 MPa
27600 psi
ASTM D638
SABIC Innovative Plastics LNP VERTON PV007 PA 6
LNP* VERTON* PV007 is a compound based on Nylon 6 resin containing 35% Long Glass Fiber. Added feature of this grade is: Structural.
Tensile Strength at Break 190 MPa
27600 psi
ISO 527-93
Wellman Wellamid® GF33A099-HRN Nylon 66, 33% Glass Reinforced, Hydrolysis Resistant
All information provided by Wellman Engineered Resins.
Tensile Strength at Break 190 MPa
27600 psi
ASTM D638
A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66
Information provided by A. Schulman.
Tensile Strength at Break 190 MPa
27600 psi
dry; ISO 527-1/-2
EMS-Grivory Grivory® LV-65H SST black 9288 PA12-GF65
Product description: Grilamid LV-65H SST black 9288 is a 65% glass fiber reinforced, heat stabilized engineering thermoplastic based on polyamide 12, designed for complex structural parts with the f..
Tensile Strength at Break 190 MPa
27600 psi
dry; ISO 527-1/-2
EMS-Grivory Grivory® LV-65H SST nat PA12-GF65
Product description: Grilamid LV-65H SST natural is a 65% glass fiber reinforced, heat stabilized engineering thermoplastic based on polyamide 12, designed for complex structural parts with the foll..
Tensile Strength at Break 190 MPa
27600 psi
dry; ISO 527-1/-2
EMS-Grivory Grivory® TSG-30/4 W PA666-GF30
Product description: Grilon TSG-30/4 W is a high heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 30% glass fibers, modified for parts with high thermal demands. Grilon TSG-..
Tensile Strength at Break 190 MPa
27600 psi
DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® 73G35HSL BK262 Nylon 6  (Unverified Data**)
35% Glass Reinforced Heat Stabilized Polyamide 6 Zytel 73G35HSL BK262 is a 35% glass fiber reinforced heat stabilized black polyamide 6 resin for injection molding.Information provided by DuPont Per..
Tensile Strength at Break 190 MPa
27600 psi
5 mm/min; ISO 527
Eurostar Staramide ACF4 PA66, 20% Carbon Fiber Reinforced, Heat stabilized, Injection Molding
Staramide ACF3 is a 20% Carbon Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Tensile Strength at Break 190 MPa
27600 psi
dry; ISO 527-1/-2
EMS-Grivory Grivory® LBV-65H FWA black 9225 PA12-GF65
Product description: Grilamid LBV-65H FWA black 9225 is a 65% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features High stiffness combined..
Tensile Strength at Break 190 MPa
27600 psi
5 [mm/min]; ISO 527-1/2
Akro-Plastic Akromid® T1 GF 30 9 (3498) PPA Conditioned, 30% Glass Filled
The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high..
Tensile Strength at Break 190 MPa
27600 psi
ISO 527
BASF Ultramid® 1503-2F BK ND 3007 33% Glass Filled PA 66 (Dry)
Description: Ultramid 1503-2F BK ND3007 is a 33% glass reinforced, heat stabilized injection molding PA6/6 grade. It is designed to provide enhance hydroysis resistance for under-the-hood applicatio..
Tensile Strength at Break 190 MPa
27600 psi
5mm/min; ISO 527-2/1A
Celanese FORTRON MT9140L6 PPS, 40% Medical Technology
Fortron MT9140L6 is a 40% glass fiber reinforced injection molding grade with a low melt viscosity. It exhibits excellent heat and chemical resistance, inherent flame retardancy and shows high hardn..
Tensile Strength at Break 190 MPa
27600 psi
5 mm/min; ISO 527-2/1A
Celanese FORTRON® 9140L6 40% Glass Reinforced Polyphenylene Sulfide (PPS)
Description: Fortron 9140L6 is a 40% glass fiber reinforced injection molding grade with a low melt viscosity. It exhibits excellent heat and chemical resistance, inherent flame retardancy and shows..
Tensile Strength at Break 190 MPa
27600 psi
DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® 70G30HSL BK039B Nylon 66  (Unverified Data**)
30% Glass Reinforced Heat Stabilized Polyamide 66 Information provided by DuPont Performance Polymers
Tensile Strength at Break 190 MPa
27600 psi
Radici Radilon® A RV330 (dry) Nylon 66
Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov..
Tensile Strength at Break 190 MPa
27600 psi
ASTM D638
SABIC Innovative Plastics LNP VERTON PV007 PA 6 (Asia Pacific)
LNP* Verton* PV007 is a compound based on Nylon 6 resin containing Long Glass Fiber.
Tensile Strength at Break 190 MPa
27600 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP Verton PV007SV_YW8D151 PA 6
Preliminary data for 35% long fiber single pellet color filled PA6This data was supplied by SABIC-IP for the Americas region.