- Polymer Property : Tensile Strength at Break = 190 MPa
Polymer Property : Tensile Strength at Break = 190 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 190 MPa | 27600 psi | ISO 37 |
| Polyplastic Armamid® PA GF50-1 Nylon 6, 50% Glass Fiber High stiffnessInformation provided by PolyPlastic Group. |
|||
| Tensile Strength at Break | 190 MPa @Temperature 23.0 °C |
27600 psi @Temperature 73.4 °F |
ISO 527-2 |
| Solvay Specialty Polymers Amodel® AE-8133 Polyphthalamide (PPA)
(discontinued **) Amodel AE-8133 is a 33% glass reinforced polyphthalamide (PPA) designed to work in the modern automotive electrical environment. This grade features a high heat deflection temperature, high flexural.. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | ISO 527-1/-2 |
| Lanxess Durethan® BKV 35 H2.0 EF 900116 Nylon 6, 35% Glass Fiber PA 6, injection molding grade, 35% glass fibers, good heat-ageing resistance, good flowability (easy flow) |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | ASTM D683 |
| Loxim 433 01HB Nylon 6,6 Information provided by Loxim Industries |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | ISO 527-1/-2 |
| Lanxess Durethan® BKV 35 H2.0 EF 901510 Nylon 6, 35% Glass Fiber PA 6, injection molding grade, 35% glass fibers, good heat-ageing resistance, good flowability (easy flow) |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | ISO 527 Type 1A |
| Solvay TECHNYL® C 216 V30 PA6, 30% glass fiber, DRY Description: Polyamide PA6, reinforced with 30 % of glass fiber, for injection molding.Available in: Asia Pacific and Latin AmericaProduct Applications: It has good mechanical properties, it is used.. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | ISO 527 Type 1A |
| Solvay TECHNYL® C 218 V 30 PA6, 30% glass fiber, DRY Description: TECHNYL® C 218 V30 is a polyamide 6, heat stabilized, reinforced with 30% of glass fiber, for injection molding. This product is available in black color.Benefits: The product offers.. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP RFN169 PA 66 LNP* LUBRICOMP* RFN169 is a compound based on Nylon 66 containing 30% Glass Fiber, 5% MOS2. Added features of this grade include: Wear Resistant, Flame Retardant. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP UFL36AS PPA (Europe-Africa-Middle East) LNP* LUBRICOMP* UFL36AS is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE. Added features include Internally Lubricated, Heat Stabilized. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Lubricomp UFL36ASP PPA (Europe-Africa-Middle East) LNP* LUBRICOMP* UFL36ASP is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE.
Added features include Internally Lubricated, Heat Stabilized.This data was supplied by SABIC-IP f.. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | |
| SGL Carbon Group PANOX® SA C063 EEA High performance oxidized textile fiber, Crimped staple fiber, For carbon/carbon and spinning PANOX® is the industry standard when it comes to fire-retardant textile fibers. As an oxidized, thermally stabilized polyacrylonitrile (PAN) fiber that will not burn, melt, soften or drip, PANOX .. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | |
| SGL Carbon Group PANOX® SA T320 EEA High performance oxidized textile fiber, Continuous Tow with 320k filaments For carbon/carbon and spinning. PANOX® is the industry standard when it comes to fire-retardant textile fibers. As an oxidized, thermally stabilized polyacrylonitrile (PAN) fiber that will not b.. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | ISO 527-2 |
| Solvay Specialty Polymers Amodel® AT-1125 HS Polyphthalamide (PPA), 25% Glass Fiber (Dry) Amodel® AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional s.. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | ASTM D638 |
| A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66 Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | ASTM D638 |
| A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66 Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | ISO 527-1/-2 |
| DSM Stanyl® TW271F6 (DAM) Nylon 46 30% Glass Reinforced, Heat Stabilized, PTFE Lubricated (North America) Information provided by DSM Engineering Plastics. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | dry; ISO 527-1/-2 |
| EMS-Grivory Grivory® LV-65H SST nat PA12-GF65 Product description: Grilamid LV-65H SST natural is a 65% glass fiber reinforced, heat stabilized engineering thermoplastic based on polyamide 12, designed for complex structural parts with the foll.. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | dry; ISO 527-1/-2 |
| EMS-Grivory Grivory® TSG-30/4 W PA666-GF30 Product description: Grilon TSG-30/4 W is a high heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 30% glass fibers, modified for parts with high thermal demands. Grilon TSG-.. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | dry; ISO 527-1/-2 |
| EMS-Grivory Grivory® TSG-35/4 W black 9832 PA666-GF35 Product description: Grilon TSG-35/4 W is a high heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 35% glass fibers, modified for parts with high thermal demands. Grilon TSG-.. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | DAM; ISO 527-1/-2 |
| DuPont Performance Polymers Zytel® 73G30HSL BK416 Nylon 6
(Unverified Data**) 30% Glass Reinforced Heat Stabilized Polyamide 6 Zytel 73G30HSL BK416 is a 30% glass fiber reinforced heat stabilized lubricated black polyamide 6 resin for injection molding.Information provided by.. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | DAM; ISO 527-1/-2 |
| DuPont Performance Polymers Zytel® 73G35HSL BK262 Nylon 6
(Unverified Data**) 35% Glass Reinforced Heat Stabilized Polyamide 6 Zytel 73G35HSL BK262 is a 35% glass fiber reinforced heat stabilized black polyamide 6 resin for injection molding.Information provided by DuPont Per.. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | ISO 527-1/-2 |
| DSM Arnite® AV2 372 PET-35% Glass Reinforced (European and Asian Grade) Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame .. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | dry; ISO 527-1/-2 |
| EMS-Grivory Grivory® LBV-65H FWA nat PA12-GF65 Product description: Grilamid LBV-65H FWA natural is a 65% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: High stiffness combined w.. |
|||
| Tensile Strength at Break | 190 MPa @Temperature -40.0 °C |
27500 psi @Temperature -40.0 °F |
ASTM D638 |
| Celanese CELANEX 3300FC PBT, 30% Glass Reinforced Celanex 3300FC is a general purpose, 30% glass reinforced, polybutylene terephthalate that offers a superior combination of mechanical, electrical, and thermal properties. This grade provides outsta.. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | 5mm/min; ISO 527-2/1A |
| Celanese FORTRON 1140LC6 PPS, 40% Specialty Fortron 1140LC6 is a 40% glass fiber reinforced material with a total chlorine content less than or equal to 900 ppm*. It offers excellent physical properties similar to those of the Fortron 1140L6.. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | 5 mm/min; ISO 527-2/1A |
| Celanese FORTRON® 9140L6 40% Glass Reinforced Polyphenylene Sulfide (PPS) Description: Fortron 9140L6 is a 40% glass fiber reinforced injection molding grade with a low melt viscosity. It exhibits excellent heat and chemical resistance, inherent flame retardancy and shows.. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP VERTON RVN17SXS PA 66 (Europe-Africa-Middle East) LNP* VERTON* RVN17SXS is a compound based on PA 66 resin containing Long Glass Fiber, MoS2. Added features include; Wear Resistant. |
|||
| Tensile Strength at Break | 190 MPa | 27600 psi | 5mm/min; ISO 527-2/1A |
| Celanese VECTRA MT1310 LCP, 30% Medical Technology The Standard for the Industry. Excellent balance of properties, including easy flow, easy processing, thermal stability, chemical resistance, mechanical and electrical properties. Suitable for vapo.. |
|||
| Tensile Strength at Break | 190 MPa @Temperature -40.0 °C |
27500 psi @Temperature -40.0 °F |
ASTM D638 |
| Celanese Celanex® 3300D PBT, 30% Glass Reinforced
(Unverified Data**) Celanex 3300D is a general purpose, 30% glass reinforced, polybutylene terephthalate that offers a superior combination of mechanical, electrical, and thermal properties. This grade provides outsta.. |
|||
| Tensile Strength at Break | 190 MPa | 27500 psi | ASTM D 638 |
| RTP Company RTP 2299 X 115088 F Polyetheretherketone (PEEK), Glass Fiber - Carbon Nanotube - ESD Protection |
|||