- HOME
- POLYMER SEARCH
- Polymer Property : Tensile Strength at Break = 6240 psi
Polymer Property : Tensile Strength at Break = 6240 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 |
| Polimeri Europa Edistir N 1782 Polystyrene General purpose polystyrene with good flow and high heat resistance. Suggested for direct gassing extrusion of heavy gage insulating boards (XPS) and in blend with high concentration of clear SBS f.. |
|||
| Tensile Strength at Break | <= 43.0 MPa | <= 6240 psi | ISO/R527 |
| Polykemi AB POLYabs S00 AS UV ABS, High Flow, UV-Stabilized, Antistatic Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Cycoloy® CY5000 PC+ABS (Asia Pacific) Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow for a wide variety of thin wall or large size applicat.. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Cycoloy® CY5005 PC+ABS Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow for a wide variety of thin wall or large size applicat.. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Cycoloy® CY5005 PC+ABS (Europe-Africa-Middle East) Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow for a wide variety of thin wall or large size applicat.. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Cycoloy® CY6010 PC+ABS (Europe-Africa-Middle East) Cycoloy CY6010 resin is a flame retardant PC/ABS blend featuring excellent flow together with good impact and UL-94 V0 listing at 1.5mm. Its excellent flow combined with balanced heat and good pract.. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Cycoloy® XP7560 ASA (Europe-Africa-Middle East) GELOY XP7560 is a general purpose ASA/PC injection moulding grade, available in various colours. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP DL002P PC (Asia Pacific) LNP LUBRICOMP* DL002P is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Exceptional Processing. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics GELOY XP7560 ASA (Europe-Africa-Middle East) GELOY XP7560 is a general purpose ASA/PC injection moulding grade, available in various colours. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ISO 37 |
| Huntsman AVALON® 60 DB Thermoplastic Polyurethane Introduction: AVALON 60 DB is a high performance polyester based thermoplastic polyurethane for injection molding. AVALON 60 DB is part of the AVALON Perform Range and offers a premium soling materi.. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ISO R 527 |
| Fainplast Compounds RKT 736/K1 Rigid PVC, Extrusion Lead Free Transparent profiles |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP DL0049EF PC LNP* Lubricomp* DL0049EF is a compound based on Polycarbonate resin containing 20% PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP DL0049EF PC (Asia Pacific) LNP* Lubricomp* DL0049EF is a compound based on Polycarbonate resin containing PTFE, Flame Retardant. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Lubricomp DP0039 PC LNP* Lubricomp* DP0039 is a Polycarbonate base resin containing PTFE and Silicone lubricants. Characteristics are: Flame Retardant.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP DP003EH PC LNP LUBRICOMP* DP003EH is a compound based on Polycarbonate resin containing 15% PTFE/Silicone. Added features of this material include: Easy Molding, Internally Lubricated, Healthcare. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP DX98306H PC (Asia Pacific) LNP* Lubricomp* DX98306H is a compound based on Polycarbonate resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Lubricomp WL0049XF PBT LNP* Lubricomp* WL0049 is a compound based on Polybutylene Terephalate resin containing PTFE and Flame Retardant. Added features include: Internally Lubricated, Flame Retardant.This data was suppl.. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 (Asia Pacific) LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 (Europe-Africa-Middle East) LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ISO 527 |
| SABIC Innovative Plastics LNP Stat-kon DEP32XXC PC (Asia Pacific) LNP* STAT-KON* DEP32XXC is a compound based on Polycarbonate resin containing PTFE, Silicone, Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied b.. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Xenoy® 5720U PBT+PC Unfilled PBT+PC alloy. Outstanding low temperature impact/chemical resistance. UV stabilized version of XENOY |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ISO 527 |
| SABIC Innovative Plastics LNP STAT-LOY AF306 ABS LNP* STAT-LOY* AF306 is a compound based on ABS resin containing 30% Glass Fiber. Added feature of this material is: Antistatic. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ISO 527 |
| SABIC Innovative Plastics LNP Stat-loy K3000 Acetal Copoly LNP* Stat-loy* K3000 is a compound based on Acetal Copolymer resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americas regi.. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP WX93111 PBT (Europe-Africa-Middle East) LNP* THERMOCOMP* WX93111 is a compound based on Polybutylene Terephalate resin containing Flame retardant , Glass Fiber, Proprietary filler. Added features include : Improved CTI. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® V3900WX PBT+PC PBT/PC blend - Unreinforced - Flame Retardant. This is a UV-stabilized grade designed for outdoor enclosure applications requiring UL 746C F1 weatherability performance. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Xenoy® X6320 PBT+PC (Asia Pacific) X6320 is a mineral filled PBT/PC resin developed for automotive painted doorhandles. Key advantages are excellent surface finish, easy processing and paint quality. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ASTM D638 |
| Eastman Eastar AN011 Copolyester Eastar AN011 copolyester is a high flow product. Eastar AN011 flow lengths are increased 20-40% relative to Eastar AN001 as shown by spiral flow testing. Other outstanding features of Eastar are eas.. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ASTM D638 |
| Asahi Glass Fluon® LM-720AP LM-ETFE Fluororesin Fluon®LM-ETFE combines the excellent properties in heat resistance and other mechanical properties owned by ETFE resin and the low melting point.Information provided by Asahi Glass Company, Inc. |
|||
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ISO R 527 |
| Fainplast Compounds RKT 736 Rigid PVC, Extrusion Lead Free Transparent antishock profiles |
|||
Copyright © lookpolymers.com All Rights Reserved