Polymer Property : Tensile Strength at Break = 71.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	<= 71.0 MPa	<= 10300 psi	ISO/R527
Polykemi AB SCANMID 6 B12^ NH9 Nylon 6, Flame Retardant, Halogen Free Information provided by Polykemi AB
Tensile Strength at Break	<= 71.0 MPa	<= 10300 psi	ISO/R527
Polykemi AB SCANMID 6 B12^ NH9L Nylon 6, Flame Retardant, Halogen Free Information provided by Polykemi AB
Tensile Strength at Break	71.0 MPa	10300 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 4501 PPC (Asia Pacific) High heat resistant polyphthlate carbonate, provides DTUL of 290F at 264 psi.
Tensile Strength at Break	71.0 MPa	10300 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® FXD941A PC (Europe-Africa-Middle East) Transparent/translucent PC for light diffusion special effects. Color package may affect performance.
Tensile Strength at Break	71.0 MPa	10300 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HPH4504H PPC (Asia Pacific) High heat specialty polycarbonate with enhanced autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 of USP Class VI). EtO, ..
Tensile Strength at Break	71.0 MPa	10300 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® HPH4504H PPC (Europe-Africa-Middle East) High heat specialty polycarbonate with enhanced autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 of USP Class VI). EtO, ..
Tensile Strength at Break	71.0 MPa	10300 psi	50 mm/min; ISO 527
SABIC Innovative Plastics LNP COLORCOMP J1000R PES (Europe-Africa-Middle East) LNP* COLORCOMP* J1000R is a compound based on Polyethersulfone resin. Added features include : Mold Release
Tensile Strength at Break	71.0 MPa	10300 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DFL32 PC LNP LUBRICOMP* DFL32 is a compound based on Polycarbonate resin containing 10% Glass Fiber and 15% PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	71.0 MPa	10300 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® ML5472 PC Gamma sterilization resistant. High heat (PPC). Available in natural color only. Internal mold release.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	71.0 MPa	10300 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® SLX1432 PC Copolymer (Asia Pacific) Medium viscosity PC copolymer with enhanced UV stabilization and added release agent. Available in opaque colors. Typical minimum color tolerance limit is DE CMC < 1.0
Tensile Strength at Break	71.0 MPa	10300 psi	ASTM D638
LG Chemical LUCON PO-3000 Electrically Conductive Thermoplastic LG Chemicals has formulated a diverse range of LUCON thermoplastic compounds containing conductive additives, such as carbon powder, (nickel coated) carbon fiber, or stainless steel fiber for solvin..
Tensile Strength at Break	71.0 MPa	10300 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP MFL36S PP LNP* LUBRICOMP* MFL36S is a compound based on Polypropylene resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant.
Tensile Strength at Break	71.0 MPa	10300 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP MFL36S PP (Asia Pacific) LNP* Lubricomp* MFL36S is a compound based on Polypropylene resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized.
Tensile Strength at Break	71.0 MPa	10300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RAP22 PA 66 LNP* LUBRICOMP* RAP22 is a compound based on Nylon 66 resin containing 10% Aramid, 10% PTFE/Silicone. Added feature of this grade includes: Wear Resistant.
Tensile Strength at Break	71.0 MPa	10300 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RL004 PA 66 LNP* LUBRICOMP* RL004 is a copmpound based on Nylon 66 resin containing 20% PTFE. Added feature of this grade includes: Wear Resistant.
Tensile Strength at Break	71.0 MPa	10300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RX85514 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RX85514 is a compound based on Nylon 66 resin containing Proprietary Filler(s).
Tensile Strength at Break	71.0 MPa	10300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP AF004 ABS (Europe-Africa-Middle East) LNP* THERMOCOMP* AF004 is a compound based on Acrylonitrile Butadiene Styren resin containing Glass Fiber.
Tensile Strength at Break	71.0 MPa	10300 psi	ISO 527-2/50
Styron CALIBREâ„¢ 200-10 Polycarbonate Resin Overview: CALIBREâ„¢ 200-10 Series are produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. They provide excellent impact resistance, heat distor..
Tensile Strength at Break	71.0 MPa	10300 psi	ISO 527-2/50
Styron CALIBREâ„¢ 201-10 Polycarbonate Resin Overview: CALIBREâ„¢ 201-10 is produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. It provides excellent impact resistance, heat distortion resi..
Tensile Strength at Break	71.0 MPa	10300 psi	ISO 527-2/50
Styron CALIBREâ„¢ 301-15 Polycarbonate Resin Overview: CALIBREâ„¢ 300-115 polycarbonate resins offer exceptional impact resistance, heat distortion resistance and optical clarity. The CALIBREâ„¢ 300-10 series products are available in 4 ..
Tensile Strength at Break	71.0 MPa	10300 psi	ISO 527-2/50; ASTM D638
Styron CALIBREâ„¢ 303V-10 Polycarbonate Resin Overview: CALIBREâ„¢ 300V-10 Polycarbonate resins offer exceptional impact resistance, heat distortion resistance, optical clarity and meets UL94 V-2 rating. CALIBRE 300V series products are avai..
Tensile Strength at Break	71.0 MPa	10300 psi	ISO 527-2/50
Styron CALIBREâ„¢ 303V-15 Polycarbonate Resin Overview: CALIBREâ„¢ 300V-15 Series Polycarbonate resins offer exceptional impact resistance, heat distortion resistance, optical clarity and meets UL94 V-2 rating. CALIBRE 300V series products a..
Tensile Strength at Break	71.0 MPa	10300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM 9085 PEI Blend High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution.
Tensile Strength at Break	71.0 MPa	10300 psi	50 mm/min; ASTM D638
Styron CALIBREâ„¢ 300-10 Polycarbonate Resin Overview: CALIBREâ„¢ 300-10 polycarbonate resin offer exceptional impact resistance, heat distortion resistance, and optical clarity. The CALIBREâ„¢ 300-10 series products are available in 4 a..
Tensile Strength at Break	71.0 MPa	10300 psi	50 mm/min; ASTM D638
Styron CALIBREâ„¢ 302-10 Polycarbonate Resin Overview: CALIBREâ„¢ 300-10 polycarbonate resins offer exceptional impact resistance, heat distortion resistance and optical clarity as well as high melt strength for blow molding and sheet appli..
Tensile Strength at Break	71.0 MPa	10300 psi	ISO 527-2/50
Styron CALIBREâ„¢ 302V-10 Polycarbonate Resin Overview: CALIBREâ„¢ 300V Polycarbonate resins offer exceptional impact resistance, heat distortion resistance, optical clarity and meets UL94 V-2 rating. CALIBRE 300V series products are availab..
Tensile Strength at Break	71.0 MPa	10300 psi	ISO 527-2/50
Styron CALIBREâ„¢ 302V-15 Polycarbonate Resin Overview: CALIBREâ„¢ 300V-15 Series Polycarbonate resins offer exceptional impact resistance, heat distortion resistance, optical clarity and meets UL94 V-2 rating. CALIBRE 300V series products a..
Tensile Strength at Break	71.0 MPa	10300 psi	DIN EN ISO 527
Wolf Kunststoff ZEDEX® ZX-410V7T A4T Polymer Alloy, Fiber Reinforced, Friction Modified Main Characteristics: Fiber-reinforced; Friction-modified; Very high stiffness (higher than that of fiber-reinforced PEEK); Very low thermal expansion coefficient; Low friction; High wear resistance..
Tensile Strength at Break	71.0 MPa	10300 psi	5mm/min; ASTM D638
Denka TX-400S Transparent Resin Polymer (MS resin) Methyl Methacrylate Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a..
Tensile Strength at Break	71.0 MPa	10300 psi	ASTM D638
Aclo Accutech ABS ABS831G20L Glass Reinforced