Wolf Kunststoff ZEDEX® ZX-410V7T A4T Polymer Alloy, Fiber Reinforced, Friction Modified

Category Polymer , Thermoplastic
Manufacturer Wolf Kunststoff
Trade Name ZEDEX®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Wolf Kunststoff ZEDEX® ZX-410V7T A4T Polymer Alloy, Fiber Reinforced, Friction Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Main Characteristics: Fiber-reinforced; Friction-modified; Very high stiffness (higher than that of fiber-reinforced PEEK); Very low thermal expansion coefficient; Low friction; High wear resistance up to 200 ° CApplications: Handling; Shipbuilding; Automitve Technology; Machine Tools; Drive Technology; Railway TechnologyInformation provided by Zedex
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 0.40 %

@Temperature 23.0 °C
0.40 %

@Temperature 73.4 °F
RMC 93%; DIN EN ISO 62
Moisture Absorption at Equilibrium 1.2 %
1.2 %
DIN EN ISO 62
Mechanical Properties Metric English Comments
Hardness, Shore A >= 100
>= 100
DIN 53505
Hardness, Shore D 90
90
DIN 53505
Ball Indentation Hardness 146 MPa
21200 psi
DIN 2039
Tensile Strength at Break 71.0 MPa
10300 psi
DIN EN ISO 527
Tensile Strength 71.0 MPa
10300 psi
DIN EN ISO 527
Tensile Stress 51.0 MPa

@Strain 1.00 %,
Time 3.60e+6 sec
7400 psi

@Strain 1.00 %,
Time 1000 hour
DIN 53444
Tensile Strength, Yield 42.4 MPa
6150 psi
Elastic Limit
Elongation at Break 4.5 %
4.5 %
Flexural; DIN EN ISO 178
4.5 %
4.5 %
DIN EN ISO 527
Elongation at Yield 1.8 %
1.8 %
Elastic Yield Point
4.5 %
4.5 %
Elongation at Maximum Force; DIN EN ISO 527
4.8 %
4.8 %
Flexural; DIN EN ISO 178
Tensile Modulus 5.499 GPa
797.6 ksi
DIN EN ISO 527
Flexural Strength 129 MPa
18700 psi
Outer Fiber Stress at 3.5% Outer Fiber Strain; DIN EN ISO 178
136.4 MPa
19780 psi
DIN EN ISO 178
138 MPa
20000 psi
DIN EN ISO 178
Flexural Modulus 5.545 GPa
804.2 ksi
DIN EN ISO 178
Compressive Yield Strength 132 MPa
19100 psi
DIN EN ISO 604
Compressive Strength 100 MPa
14500 psi
Elastic Limit
133 MPa
19300 psi
break; DIN EN ISO 604
135 MPa
19600 psi
DIN EN ISO 604
70.0 MPa

@Time 3.60e+7 sec
10200 psi

@Time 10000 hour
96.0 MPa

@Time 360000 sec
13900 psi

@Time 100 hour
108 MPa

@Time 36.0 sec
15700 psi

@Time 0.0100 hour
129 MPa

@Strain 3.50 %
18700 psi

@Strain 3.50 %
DIN EN ISO 604
Compressive Modulus 6.30 GPa
914 ksi
DIN EN ISO 604
Fatigue Strength 59.0 MPa

@# of Cycles 1.00e+6
8560 psi

@# of Cycles 1.00e+6
1 Hz
K Factor (ISO) 0.20 µm/km

@Temperature 20.0 °C
0.20 µm/km

@Temperature 68.0 °F
0.90 µm/km

@Temperature 100 °C
0.90 µm/km

@Temperature 212 °F
1.0 µm/km

@Temperature 200 °C
1.0 µm/km

@Temperature 392 °F
Charpy Impact Unnotched 3.00 J/cm²
14.3 ft-lb/in²
EN ISO 179/1eU
Charpy Impact, Notched 1.12 J/cm²
5.33 ft-lb/in²
EN ISO 179/1eA
Coefficient of Friction, Dynamic 0.16

@Temperature 20.0 °C
0.16

@Temperature 68.0 °F
Dry Operation
0.17

@Temperature 100 °C
0.17

@Temperature 212 °F
Dry Operation
Coefficient of Friction, Static 0.23

@Temperature 20.0 °C
0.23

@Temperature 68.0 °F
Dry Operation
Tensile Creep Modulus, 1000 hours 5260 MPa
763000 psi
At 1% Deformation; DIN 53444
Limiting Pressure Velocity 0.300 MPa-m/sec
8570 psi-ft/min
v = 1m/min
0.500 MPa-m/sec
14300 psi-ft/min
v = 100m/min
0.600 MPa-m/sec
17100 psi-ft/min
v = 10m/min
1.667 MPa-m/sec
47580 psi-ft/min
v = 200m/min
Compression Set 2.2 %
2.2 %
Elastic Compression Limit
5.2 %
5.2 %
Nominal Compressive Yield Strain; DIN EN ISO 604
5.2 %
5.2 %
Nominal Compressive Strain at Compressive Strength; DIN EN ISO 604
39 %
39 %
Nominal Compressive Strain at Break; DIN EN ISO 604
Thermal Properties Metric English Comments
CTE, linear 23.0 µm/m-°C

@Temperature <=100 °C
12.8 µin/in-°F

@Temperature <=212 °F
ISO E 830
25.0 µm/m-°C

@Temperature <=150 °C
13.9 µin/in-°F

@Temperature <=302 °F
ISO E 831
Specific Heat Capacity 0.870 J/g-°C
0.208 BTU/lb-°F
DSC
Melting Point 315 °C
599 °F
DSC
Maximum Service Temperature, Air 150 °C
302 °F
Pressed Bushings
190 °C
374 °F
Continuous
200 °C
392 °F
Short Term (3h)
Deflection Temperature at 1.8 MPa (264 psi) 206 °C
403 °F
DIN EN ISO 75
Glass Transition Temp, Tg 211 °C
412 °F
DSC
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 3.60e+6 ohm-cm
3.60e+6 ohm-cm
IEC 93
Surface Resistance 3.00e+6 ohm
3.00e+6 ohm
IEC 93
Dielectric Constant 3.3

@Frequency 110 Hz
3.3

@Frequency 110 Hz
IEC 250
Dielectric Strength 0.100 kV/mm
2.54 kV/in
IEC 243
Dissipation Factor 0.00070
0.00070
IEC 112
0.083

@Frequency 1.00 Hz
0.083

@Frequency 1.00 Hz
Descriptive Properties Value Comments
Alignment Adjustment 2
Nominal Scale: 1, low; 10, high
Chemical Sterilization 4
Nominal Scale: 1, low; 10, high
Color Black
Creep Resistance 7
Nominal Scale: 1, low; 10, high
Dimensional Stability with Thermal Expansion 9
Nominal Scale: 1, low; 10, high
Free from Silicon Applicable
Gamma-rays Radiation Sterilization 7
Nominal Scale: 1, low; 10, high
Injection Molded Parts Applicable
Machined Parts Applicable
Moist Heat Sterilization 7
Nominal Scale: 1, low; 10, high
Plastic Granules Applicable
Resistance Against dust, Dirt, Abrasive Substances 7
Nominal Scale: 1, low; 10, high
Resistance Against Hot Water 130
Resistance to Chemicals 5
Nominal Scale: 1, low; 10, high
Resistant Against Disinfectant Applicable
Rods up to Øe (de) Applicable
Sheets up to Maximum Thickness Applicable
Sliding Velocity 100
Suitable for Outdoor Use 8
Nominal Scale: 1, low; 10, high
Tubes (hollow rods) up to Øe (de) Applicable
UV Rays Resistance 9
Nominal Scale: 1, low; 10, high
UV-Sterilization 10