- Polymer Property : Tensile Strength at Break = 225 MPa
Polymer Property : Tensile Strength at Break = 225 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | >= 225 MPa @Temperature 200 °C |
>= 32600 psi @Temperature 392 °F |
|
| PEAK Werkstoff DISPAL S541 Aluminum Alloy, AlMg6Mn4SiTiZr, Condition F Information provided by PEAK Werkstoff GmbH |
|||
| Tensile Strength at Break | 225 MPa @Temperature 23.0 °C |
32600 psi @Temperature 73.4 °F |
|
| LATI Laramid G/35 PPA, 35% Glass Fiber Reinforced Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; .. |
|||
| Tensile Strength at Break | 225 MPa @Temperature 90.0 °C |
32600 psi @Temperature 194 °F |
|
| LATI Larpeek 10 K/30 PEEK, 30% Carbon Fiber Reinforced Polyetheretherketone (PEEK) based compound. Carbon fiber. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; As.. |
|||
| Tensile Strength at Break | 225 MPa @Temperature 23.0 °C |
32600 psi @Temperature 73.4 °F |
|
| LATI Larpeek 50 K/30 PEEK, 30% Carbon Fiber Reinforced Polyetheretherketone (PEEK) based compound. Carbon fiber. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; As.. |
|||
| Tensile Strength at Break | 225 MPa @Temperature 23.0 °C |
32600 psi @Temperature 73.4 °F |
|
| LATI Larpeek 10 G/60 PEEK, 60% Glass Fiber Reinforced Polyetheretherketone (PEEK) based compound. Glass fibers. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; As.. |
|||
| Tensile Strength at Break | 225 MPa @Temperature 60.0 °C |
32600 psi @Temperature 140 °F |
|
| LATI Latigloss 57 G/50 F2 PPA, 50% Glass Fiber Reinforced Product with high mechanical properties and exceptional surface finish based on Semi-aromatic polyamide (PPA). Glass fibers. Potentially suitable for food/medical contact application. Availability: .. |
|||
| Tensile Strength at Break | 225 MPa @Temperature 23.0 °C |
32600 psi @Temperature 73.4 °F |
3; ISO 527-2 |
| Solvay Specialty Polymers Amodel® A-4145 HH Polyphthalamide (PPA), 45% Glass Fiber (Dry) Amodel® A-4145 HH is a 45% glass fiber reinforced heat stabilized grade of polyphthalamide (PPA) that has been designed to provide outstanding property retention to thermal oxidative degradation .. |
|||
| Tensile Strength at Break | 225 MPa @Temperature 23.0 °C |
32600 psi @Temperature 73.4 °F |
DAM; ISO 527 |
| DuPont Performance Polymers Zytel® 70G43HSLA BK099 Nylon 66
(Unverified Data**) Zytel® 70G43HSLA BK099 is a 43% glass fiber reinforced, heat stabilized, black polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers |
|||