PEAK Werkstoff DISPAL S541 Aluminum Alloy, AlMg6Mn4SiTiZr, Condition F

Category Metal , Nonferrous Metal , Aluminum Alloy
Manufacturer PEAK Werkstoff
Trade Name DISPAL
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PEAK Werkstoff DISPAL S541 Aluminum Alloy, AlMg6Mn4SiTiZr, Condition F.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by PEAK Werkstoff GmbH
Physical Properties Metric English Comments
Density 2.584 - 2.856 g/cc
0.09335 - 0.1032 lb/in³
Mechanical Properties Metric English Comments
Hardness, Vickers >= 130
>= 130
HV30
Tensile Strength at Break >= 95.0 MPa

@Temperature 300 °C
 >= 13800 psi

@Temperature 572 °F
>= 161 MPa

@Temperature 250 °C
 >= 23400 psi

@Temperature 482 °F
>= 225 MPa

@Temperature 200 °C
 >= 32600 psi

@Temperature 392 °F
>= 313 MPa

@Temperature 150 °C
 >= 45400 psi

@Temperature 302 °F
>= 411 MPa

@Temperature 100 °C
 >= 59600 psi

@Temperature 212 °F
>= 435 MPa

@Temperature 20.0 °C
 >= 63100 psi

@Temperature 68.0 °F
Tensile Strength, Yield >= 56.0 MPa

@Temperature 300 °C
 >= 8120 psi

@Temperature 572 °F
>= 114 MPa

@Temperature 250 °C
 >= 16500 psi

@Temperature 482 °F
>= 182 MPa

@Temperature 200 °C
 >= 26400 psi

@Temperature 392 °F
>= 251 MPa

@Temperature 150 °C
 >= 36400 psi

@Temperature 302 °F
>= 286 MPa

@Temperature 100 °C
 >= 41500 psi

@Temperature 212 °F
>= 305 MPa

@Temperature 20.0 °C
 >= 44200 psi

@Temperature 68.0 °F
Elongation at Break >= 5.7 %

@Temperature 20.0 °C
 >= 5.7 %

@Temperature 68.0 °F
>= 8.4 %

@Temperature 100 °C
 >= 8.4 %

@Temperature 212 °F
>= 31.2 %

@Temperature 150 °C
 >= 31.2 %

@Temperature 302 °F
>= 39.4 %

@Temperature 200 °C
 >= 39.4 %

@Temperature 392 °F
>= 45 %

@Temperature 250 °C
 >= 45 %

@Temperature 482 °F
>= 50 %

@Temperature 300 °C
 >= 50 %

@Temperature 572 °F
Modulus of Elasticity >= 41.0 GPa

@Temperature 300 °C
 >= 5950 ksi

@Temperature 572 °F
>= 55.0 GPa

@Temperature 250 °C
 >= 7980 ksi

@Temperature 482 °F
>= 58.0 GPa

@Temperature 200 °C
 >= 8410 ksi

@Temperature 392 °F
>= 64.0 GPa

@Temperature 150 °C
 >= 9280 ksi

@Temperature 302 °F
>= 70.0 GPa

@Temperature 100 °C
 >= 10200 ksi

@Temperature 212 °F
>= 77.0 GPa

@Temperature 20.0 °C
 >= 11200 ksi

@Temperature 68.0 °F
Poissons Ratio 0.324

@Temperature 20.0 °C
 0.324

@Temperature 68.0 °F
0.33

@Temperature 100 °C
 0.33

@Temperature 212 °F
0.331

@Temperature 150 °C
 0.331

@Temperature 302 °F
0.333

@Temperature 200 °C
 0.333

@Temperature 392 °F
0.336

@Temperature 300 °C
 0.336

@Temperature 572 °F
Fatigue Strength 225.8 MPa
32750 psi
P50% rotary bending values for 5X10<sup>7</sup> cycles
Shear Modulus 24.0 GPa

@Temperature 300 °C
 3480 ksi

@Temperature 572 °F
27.0 GPa

@Temperature 200 °C
 3920 ksi

@Temperature 392 °F
28.0 GPa

@Temperature 150 °C
 4060 ksi

@Temperature 302 °F
29.0 GPa

@Temperature 100 °C
 4210 ksi

@Temperature 212 °F
31.0 GPa

@Temperature 20.0 °C
 4500 ksi

@Temperature 68.0 °F
Thermal Properties Metric English Comments
CTE, linear 21.8 - 22.8 µm/m-°C

@Temperature 20.0 - 100 °C
 12.1 - 12.7 µin/in-°F

@Temperature 68.0 - 212 °F
22.6 - 23.6 µm/m-°C

@Temperature 20.0 - 200 °C
 12.6 - 13.1 µin/in-°F

@Temperature 68.0 - 392 °F
23.4 - 24.4 µm/m-°C

@Temperature 20.0 - 300 °C
 13.0 - 13.6 µin/in-°F

@Temperature 68.0 - 572 °F
Melting Point 570 - 792 °C
1060 - 1460 °F
Solidus 570.3 - 576.3 °C
1059 - 1069 °F
Liquidus 785.8 - 791.8 °C
1446 - 1457 °F
Component Elements Properties Metric English Comments
Aluminum, Al 87 %
87 %
As Balance
Magnesium, Mg 6.0 %
6.0 %
Manganese, Mn 4.0 %
4.0 %
Silicon, Si 1.0 %
1.0 %
Titanium, Ti 1.0 %
1.0 %
Zirconium, Zr 1.0 %
1.0 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000880 - 0.00000970 ohm-cm
0.00000880 - 0.00000970 ohm-cm