Polymer Property : Film Tensile Strength at Break, MD = 24.1 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
LyondellBasell Plexar® PX2049 Extrudable Tie-Layer Resin - Anhydride Modified HDPE (discontinued **) General DescriptionPLEXAR tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins a..
Film Tensile Strength at Break, MD	>= 24.1 MPa	>= 3500 psi	ASTM D 882 A
Total Finathene® 6450 HDPE film (discontinued **) Applications: overwrap, food packaging, coextrusion, extrusion coatingInformation provided provided by Total Petrochemicals.Total Petrochemicals includes former Fina and Atofina plastics product lin..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
Westlake EB561 6.5% Ethylene Vinyl Acetate Copolymer (discontinued **) Excellent sealability, excellent impact strength, good optics and enhanced stabilization.Application/UsesFrozen food packagingFresh food packagingIce bagsHeavy duty produce bagsFDA: This material co..
Film Tensile Strength at Break, MD	24.1 - 141 MPa	3500 - 20500 psi	Average value: 55.9 MPa Grade Count:113
Overview of materials for High Density Polyethylene (HDPE), Film Grade This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Film Grade". Each property range of values reported is minimum and max..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
LyondellBasell PetrotheneÂ® NA272130 Medium Density Polyethylene, Film Extrusion Grade PETROTHENE NA272130 is a medium density polyethylene resin designed for overwrap film applications. NA272130 exhibits good film optics and high stiffness.Regulatory Status: NA272130 meets the requir..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
LyondellBasell PetrotheneÂ® NA960000 Low Density Polyethylene ApplicationsPETROTHENE NA960 is a series of resins designed for a wide variety of industrial film applications where high impact strength and excellent drawdown are needed. NA960 exhibits good unif..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
LyondellBasell PetrotheneÂ® NA960070 Low Density Polyethylene ApplicationsPETROTHENE NA 960 is a series of resins designed for a wide variety of industrial film applications where high impact strength and excellent drawdown are needed. NA 960 exhibits good un..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
LyondellBasell PetrotheneÂ® NA960083 Low Density Polyethylene ApplicationsPETROTHENE NA 960 is a series of resins designed for a wide variety of industrial film applications where high impact strength and excellent drawdown are needed. NA 960 exhibits good un..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
Westlake EF378 Low Density Polyethylene WESTLAKE EF378 is suggested for cast film applications. It has excellent haze and gloss, good strength, good processability, and good heat sealability.Application/UsesDiaper linersGeneral purpose cl..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
Westlake EF412 Low Density Polyethylene WESTLAKE polyethylene EF412 is a low-density polyethylene with very good optical and strength properties. This material is an excellent choice for bakery films and food packaging applications.Applic..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
Westlake EF421 Low Density Polyethylene WESTLAKE polyethylene EF421 is a low-density polyethylene with very good optical and strength properties. This material is an excellent choice for bakery films and general purpose food packaging app..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
Westlake EF601 Low Density Polyethylene Westlake EF601 is a fractional melt LDPE with excellent toughness. It is suggested in heavy duty films and shipping sacks, and in industrial shrink applications. It can be used as a bubble stabilize..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
Westlake Elevate™ EF561 6.5% Ethylene Vinyl Acetate Copolymer Westlake EF 561 resin is a fractional melt index 6.5% EVA copolymer designed for ice bags, frozen food bags, and other films that require excellent toughness and good heat sealing characteristics. T..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
Westlake Elevate™ EF575 7.5% Ethylene Vinyl Acetate Copolymer Westlake EF 575 resin is a fractional melt index 7.5% EVA copolymer designed for ice bags, frozen food bags, and other films that require excellent toughness and good heat sealing characteristics. T..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
ExxonMobil LD 143.26 High Clarity Packaging Film Resin Product Description: LD 143.26 is a homopolymer packaging film resin with excellent clarity and good stiffness. It is suitable for processing in either blown or cast film equipment. In blown film eq..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
ExxonMobil LDPE LD 104BR Low Density Polyethylene Resin Product Description: LD 104BR is an LDPE grade, which offers good optical properties combined with increased stiffness.Availability: Africa & Middle East, Asia Pacific and Europe Additive: Antibloc..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
ExxonMobil LDPE LD 143.26 Low Density Polyethylene Resin Product Description: LD 143.26 is a homopolymer packaging film resin with excellent clarity and good stiffness. It is suitable for processing in either blown or cast film equipment. In blown film eq..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
ExxonMobil LDPE LD 150AC Low Density Polyethylene Resin Product Description: LD 150 series are LDPE grades, offering good blend mechanical properties and stiffness. Several additive packages are available according to the required surface properties.Avai..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
ExxonMobil LDPE LD 150BW Low Density Polyethylene Resin Product Description: LD 150 series are LDPE grades, offering good blend mechanical properties and stiffness. Several additive packages are available according to the required surface properties.Avai..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
ExxonMobil LDPE LD 165BW1 Low Density Polyethylene Resin (European Grade) Product Description: LD 165 series are LDPE grades, offering high strength combined with medium optical properties.Availability: Africa & Middle East and Europe Additive: Antiblock: NoSlip: NoTherm..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
ExxonMobil LDPE LD 364HE Low Density Polyethylene Resin Product Description: LD 364HE is an LDPE, offering a good combination of mechanical, optical and sealing properties.Availability: Africa & Middle East and Europe Additive: Antiblock: 1500 ppmSlip: ..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi
Dow LDPE 501I Low Density Polyethylene, Clear Film Grade DOW LDPE 501I, a barefoot resin used for bakery film and other packaging applications that require optical clarity. This material complies with U.S.FDA regulation 21 CFR 177.1520(c) 2.1 for food con..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi
Dow LDPE 503A Low Density Polyethylene, Liner Film Grade DOW LDPE 503A resin is used for liner film and other packaging applications that require optical clarity. It contains medium levels of slip additive and low levels of antiblock additive. It complies..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi
Dow LDPE 609A Low Density Polyethylene, High Clarity Film Grade DOW LDPE 609A resin is a fully formulated high strength clarity film resin for optical packaging applications, such as produce and bakery film. It contains medium levels of slip additive and low lev..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi
Dow LDPE 752A Low Density Polyethylene, Film Grade DOW LDPE 752A resin is a drawdown film resin for thin gauge applications such as garment films. It contains high levels of both slip and antiblock additives. This material complies with U.S.FDA regu..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
ExxonMobil Escorene™ FL 00206 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 00206 is a copolymer of ethylene and vinyl acetate. Processing Conditions: Processing temperatures above 280°C (536°F) may cause resin degradation. Machines should always b..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	Direction not specified
Abatron AboThane 8003-3 Polyurethane Coating AboThane 8003-3 is a clear one-package, moisture-cure polyurethane coating for hardwood, concrete and seamless floors. It was designed for high flexibility, excellent wear and antiskid properties, ..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
ExxonMobil LDPE LD 302.32 Low Density Polyethylene Resin Product Description: LD 302 resins are 3.5% vinyl acetate copolymer, high film resins. The combination of comonomer content and low melt index helps produce films which exhibit superior impact stren..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
ExxonMobil LDPE LD 302.32 Low Density Polyethylene Resin (European Grade) Product Description: LD 302 resins are 3.5% vinyl acetate copolymer, high clarity film resins. The combination of comonomer content and low melt index helps produce films which exhibit superior impa..
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
ExxonMobil LDPE LD 302.56 Low Density Polyethylene Resin Product Description: LD 302 resins are 3.5% vinyl acetate copolymer, high film resins. The combination of comonomer content and low melt index helps produce films which exhibit superior impact stren..