Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ISO 527-3 |
Polimeri Europa Flexirene® CM 50 Butene Copolymer Linear Low Density Polyethylene Flexirene CM 50 is a butene copolymer with medium density (C4-LLDPE), with antioxidants, suitable for cast film extrusion.Main Applications: Flexirene CM 50 is a highly stiff product and it is reco.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ISO 527-3 |
Polimeri Europa Riblene® FC 20 Low Density Polyethylene - Blown Film Extrusion Riblene FC 20 is a high molecular weight low density polyethylene resin (LDPE) suitable for blown film extrusion. Riblene FC 20 is characterized by a high melt strength leading to a good bubble sta.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ISO 527-3 |
Polimeri Europa Riblene® FF 20 Low Density Polyethylene - Blown Film Extrusion Riblene FF 20 is a high molecular weight low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FF 20 is characterized by a good melt strength leading to a good bubble stability.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ISO 527-3 |
Polimeri Europa Riblene® FF 24 Low Density Polyethylene - Blown Film Extrusion Riblene FF 24 is a high molecular weight low density polyethylene (LDPE), with added slip and antiblocking agents, suitable for blown film extrusion. Riblene FF 24 is characterized by a good melt s.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ISO 527-3 |
Polimeri Europa Riblene® FH 20 Low Density Polyethylene - Blown Film Extrusion Riblene FH 20 is a low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FH 20 is characterized by a good balance between processability and mechanical properties.Films manufac.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ISO 527-3 |
Polimeri Europa Riblene® FL 24 Low Density Polyethylene - Blown Film Extrusion Riblene FL 24 is a low density polyethylene (LDPE) with added slip and antiblocking agents, suitable for blown film extrusion. Riblene FL 24 is characterized by a good balance between processabilit.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® PP 1386 PRE-ELEC PP 1386 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa @Thickness 0.400 mm |
3630 psi @Thickness 0.0157 in |
ISO 527 |
Premix Thermoplastics PRE-ELEC® PP 1391 Conductive Thermoplastic Compound PRE-ELEC® PP 1391 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-E.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa @Thickness 0.400 mm |
3630 psi @Thickness 0.0157 in |
ISO 527 |
Premix Thermoplastics PRE-ELEC® PP 1397 Conductive Thermoplastic Compound PRE-ELEC® PP 1397 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-E.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM D882 |
Petroquimica Triunfo Trithene® TS 4016 LDPE and LLDPE Blend - Film The Trithene® TS 4016 resin is a mixture of low-density polyethylene (LDPE) with linear low-density polyethylene (LLDPE) designed to meet the needs of the technical films segment for the use of aut.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ISO 527-3 |
Polimeri Europa Greenflex® FD 23 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion Greenflex FD 23 is an ethylene vinyl acetate copolymer (EVA) suitable for blown film extrusion. Greenflex FD 23 is a version of Greenflex FD 20 with added slip and antiblocking agents. Films produ.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM D882 |
ExxonMobil LD 117.03 Blown Overwrap Film Resin
(discontinued **) LD 117 resins are homopolymer film resins with good clarity and excellent stiffness. Film from LD 117 resins can be used in overwrap applications and push-through type packaging equipment. Film ma.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM D882 |
ExxonMobil LD 117.08 Blown Overwrap Film Resin
(discontinued **) LD 117 resins are homopolymer film resins with good clarity and excellent stiffness. Film from LD 117 resins can be used in overwrap applications and push-through type packaging equipment. Film ma.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM D882 |
ExxonMobil Escorene® LD-104 LDPE Packaging Film Resin, High Clarity
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A homopolymer packaging film resin with excellent clarity and good stiffness. It is excellent either blown film or chill roll casting equipment. I.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM D882 |
Huntsman PE1651 EVA Film Extrusion
(discontinued **) 6.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Yields film with outstanding low temperature strength, excellent clarity, and good heat seal.Applications: Film extrusion: ice bags, liqui.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM D882 |
ExxonMobil Escorene® LD-129 MDPE Cast Overwrap Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A homopolymer film resin with good clarity and excellent stiffness. Film made from LD-129 can be used in overwrap applications and in push-through .. |
|||
Film Tensile Strength at Break, MD | 25.0 - 52.0 MPa | 3630 - 7540 psi | Average value: 36.6 MPa Grade Count:80 |
Overview of materials for Linear Low Density Polyethylene (LLDPE)/Butene, Film This property data is a summary of similar materials in the MatWeb database for the category "Linear Low Density Polyethylene (LLDPE)/Butene, Film". Each property range of values reported is minimum.. |
|||
Film Tensile Strength at Break, MD | 25.0 - 57.0 MPa | 3630 - 8270 psi | Average value: 47.0 MPa Grade Count:6 |
Overview of materials for Cyclo Olefin Polymer This property data is a summary of similar materials in the MatWeb database for the category "Cyclo Olefin Polymer". Each property range of values reported is minimum and maximum values of appropria.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM D882 |
Metabolix M-veraâ„¢ B5008 Film Grade Compostable Bioplastic B5008 is a compostable film product with 30% biobased carbon content that is ideal for compost bags and can liners used for organic waste diversion and for shopping and retail bags.Features:Meets re.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ISO 527-3 |
Borealis Borseal™ RE939CF Polypropylene Copolymer Borseal™ RE939CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications: Borseal™ RE939CF is designed for: Food packaging,.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa @Temperature 24.0 °C |
3630 psi @Temperature 75.2 °F |
22mm/min; ISO 527-3 |
Borealis FA3227 Low Density Polyethylene FA3227 is a Low Density Polyethylene for Film Extrusion. Autoclave Technology. Heat and U/V stabilized. This grade is suitable for building construction film and meets the requirements for heat, al.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ISO 527-3 |
Borealis FT3200 Low Density Polyethylene FT3200 is a Low Density Polyethylene for Film Extrusion. Applications heavy-duty bags, shrink film, construction films, and agricultural films. FT3200 contains no additives.Information provided by.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | 500 mm/min; ISO 527-3 |
DuPont Elvaloy® 3217 AC Ethylene and 17% Butyl Acrylate Copolymer Elvaloy® 3217 AC contains antioxidant, slip and antiblock additives.Elvaloy® 3217 AC has been developed for film applications requiring a combination of softness, toughness and low friction. Typi.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ISO 527-3 |
Topas Advanced Polymers TOPAS® 9903D-10 Cyclic Olefin Copolymer (COC) TOPAS® 9903D-10 is a very low glass transition temperature (Tg=33°C) film extrusion grade. It is designed to deliver high shrinkage at low temperatures in shrink packaging applications. It is a mo.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM D882 |
Braskem BC818 Extrusion Coating Low Density Polyethylene Description: BC818 is a grade produced under high pressure in an autoclave reactor. In the coating process it presents very good optical properties, low neck-in, good film stability, and good adhesi.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM-D882 |
Braskem F 7018 LDPE Extrusion Coating Polyethylene LDPE F 7018 is a low-density polyethylene and has excellent processability and sealability at low temperatures. It does not contain additives. Its applications include: extrusion coating; and injec.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM-D882 |
Braskem F7018 LDPE Injection Molding Polyethylene F7018 is a low-density polyethylene with excellent processability and sealability at low temperatures. It does not contain additives. Its applications include: extrusion coating, injection molding .. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM-D882 |
Braskem TN7006 LDPE Blown Film Extrusion Polyethylene TN7006 is a low-density polyethylene (LDPE) specially developed for coextruded films and lamination. The resin presents a great combination of mechanical, optical, and stiffness properties. TN7006 h.. |
|||
Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM D882 |
Huntsman PE1451 EVA Film Extrusion
(discontinued **) 4.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: .. |
|||
Film Tensile Strength at Break, MD | 25.0 - 33.0 MPa | 3630 - 4790 psi | Average value: 28.3 MPa Grade Count:4 |
Overview of materials for Polypropylene with Carbon Black Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with Carbon Black Filler". Each property range of values reported is minimum and maximum v.. |