Polymer Property : Film Tensile Strength at Break, MD = 8000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	55.2 - 68.9 MPa	8000 - 10000 psi	ASTM D882
Honeywell ACLAR® 22C (3.00 mil) Copolymer Film (discontinued **) Description: ACLAR® 22C is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It has moisture barrier and is used for electroluminescent lamps.Information provided by Honeywe..
Film Tensile Strength at Break, MD	55.2 - 68.9 MPa	8000 - 10000 psi	ASTM D882
Honeywell ACLAR® 22C (2.00 mil) Copolymer Film (discontinued **) Description: ACLAR® 22C is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It has moisture barrier and is used for electroluminescent lamps.Information provided by Honeywe..
Film Tensile Strength at Break, MD	55.2 MPa	8000 psi	ASTM D882
LyondellBasell PetrotheneÂ® LP510300 High Density Polyethylene ApplicationsPETROTHENE LLP 5103-00 is a copolymer resin designed for blown film applications. This resin offers high stiffness, excellent appearance and bubble stability and good drawdown. It is r..
Film Tensile Strength at Break, MD	55.2 MPa	8000 psi	ASTM D882
Westlake LF2040 Hexene Linear Low Density Polyethylene Westlake LF2040 is a hexene LLDPE with excellent physical properties and heat sealing characteristics, which allow for down-gauging and blending with other materials. Typical applications include s..
Film Tensile Strength at Break, MD	55.2 MPa	8000 psi	ASTM D882
ExxonMobil Exact™ 3040 Cast Ethylene-based Plastomer Resin Product Description: Exact 3040 is an ethylene-based hexane copolymer produced using ExxonMobil Chemical’s EXXPOL® Catalyst Technology. Exact 3040 is designed for monolayer and coextrusion cast fi..
Film Tensile Strength at Break, MD	55.2 MPa	8000 psi	ASTM D882
ExxonMobil HDPE HTA 002 High Density Polyethylene Resin Product Description: HTA 002 is a general purpose medium molecular weight HDPE grade, characterized by easy processability, especially in coextrusion and blending with other polyolefins. HTA 002 can..
Film Tensile Strength at Break, MD	>= 55.2 MPa	>= 8000 psi	ASTM D882
DuPont™ Tedlar® TWH15BL3 Low Gloss White Polyvinyl Fluoride Film Properties of DuPont™ Tedlar® polyvinyl fluoride (PVF) biaxially oriented film include excellent resistance to weathering, outstanding mechanical properties, and inertness towards a wide variety o..
Film Tensile Strength at Break, MD	55.2 MPa	8000 psi	ASTM D882
ExxonMobil NTX™ NTX 095 Super Strength Film Resin NTX super strength hexene blown film resins are designed for applications requiring exceptional strength for maximum downgauging potential. Key property improvements are significantly superior impac..
Film Tensile Strength at Break, MD	55.2 MPa	8000 psi	ASTM D882
ExxonMobil NTX™ NTX 104 Super Strength Film Resin NTX super strength hexene blown film resins are designed for applications requiring exceptional strength for maximum downgauging potential. Key property improvements are significantly superior impac..
Film Tensile Strength at Break, MD	55.2 MPa	8000 psi	ASTM D882
ExxonMobil NTX™ NTX 141 Super Strength Film Resin NTX super strength hexene blown film resins are designed for applications requiring exceptional strength for maximum downgauging potential. Key property improvements are significantly superior impac..
Film Tensile Strength at Break, MD	55.2 MPa	8000 psi	ASTM D882
ExxonMobil NTX™ NTX 150 Super Strength Film Resin NTX super strength hexene blown film resins are designed for applications requiring exceptional strength for maximum downgauging potential. Key property improvements are significantly superior impac..