Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | >= 34.0 MPa | >= 4930 psi | ASTM D638 |
NIZHNEKAMSKNEFTEKHIM PP 1500L (C30G) Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
Tensile Strength, Yield | >= 34.0 MPa | >= 4930 psi | ASTM D638 |
NIZHNEKAMSKNEFTEKHIM PP 1550J (T30S) Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
Tensile Strength, Yield | >= 34.0 MPa | >= 4930 psi | ASTM D638 |
NIZHNEKAMSKNEFTEKHIM PP 1510M (X30S) Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | 50mm/min; ASTM D638 |
Reliance Industries Repol H080EG Polypropylene REPOL Polypropylene H080EG is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly.. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | 50 mm/min |
Eastman Tenite 180A-28(HT) Cellulose Acetate
(discontinued **) 28% Plasticized.ISO data as provided by the manufacturer, Eastman Chemical. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | ISO R527 |
Fainplast Compounds RE 337 Rigid PVC, Extrusion Cheap profiles |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
LyondellBasell Pro-fax 6301 Polypropylene Homopolymer, Flake Resin Primary Processing Method: Masterbatch/ConcentratesKey Features: general purpose polypropylene homopolymer flake resin, minimal stabilization, FDA acceptableApplications: compounding, concentrates, .. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | ISO 527 |
FKuR Kunststoff Terralene® WF 6534 Biobased Polyethylene With the brand name Terralene® FKuR offers biobased polyethylene compounds made using Braskem's Green PE. When compared to conventional polyethylene (PE), the main difference is that the ethanol.. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
LG Chemical LUMAX HF-5006F High Flow PBT, Weather Resistant, Flame Retardant LUMAX resins are a family of thermoplastic blends of polybutyleneterephthalate(PBT) and styrenic resins that combine the most desirable properties of both resins and fillers. They offer high heat r.. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DZL34E PC (Asia Pacific) LNP* Lubricomp* DZL34E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP MX91206 PP LNP* Lubricomp* MX91206 is a compound based on Polypropylene containing proprietary fillers. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength, Yield | 34.0 MPa @Thickness 3.20 mm |
4930 psi @Thickness 0.126 in |
Injection Molded; ASTM D638 |
Styron LGF 7600 Polypropylene Overview: STYRON LGF7600 is intended for use injection molding applications that require high stiffness. The material has good processability and fast cycle times. It contains nucleating agent. LGF .. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON KD000EI Acetal Copolymer (Europe-Africa-Middle East) LNP* Stat-Kon* KD000EI is a compound based on Acetal Copolymer resin containing Carbon Powder. Added features include: Electrically Conductive, Impact Modified. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP AB002 ABS LNP* THERMOCOMP* AB002 is a compound based on ABS resin containing 10% Glass Bead. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP1666 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1666 is a 10% talc filled homopolymer polypropylene compound. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
A. Schulman POLYFLAM™ FPP 1007 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007 is a 40% talc filled homopolymer polypropylene compound.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | ISO 527-2 |
Total PPH 10012 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 10012 is a nucleated and antistatic homopolymer polypropylene obtained by controlled rheology.ApplicationPPH 10012 is intended for high speed injection molding of household.. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP1666 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1666 is a 10% talc filled homopolymer polypropylene compound. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
A. Schulman POLYFLAM™ FPP 1007 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007 is a 40% talc filled homopolymer polypropylene compound.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
A. Schulman POLYFLAM™ FPP 1007E Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007E is a 40% talc filled homopolymer compound for extrusion applications.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers Centrex® 813 General Purpose Injection Molding Grade ASA/AES Centrex 813 resin is a high-gloss, high-impact grade of ASA/AES, a blend of acrylonitrile-styrene-acrylate and acrylonitrile-ethylene-propylene styrene. This injection molding grade with a good bala.. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers NPP30-0500 TF20 20% Talc Filled Homopolymer Polypropylene Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM-D638 |
Braskem H 503HS HOMO Polypropylene Homopolymer H 503HS is a low melt flow rate homopolymer for general purpose. It is designed for raffia extrusion and fiber extrusion. This product exhibits excellent processability, high speed production with g.. |
|||
Tensile Strength, Yield | 34.0 - 55.0 MPa | 4930 - 7980 psi | ASTM D638 |
Arkema Group KYNAR® 370 Polyvinylidene Fluoride (PVDF) Homopolymer - Injection Molding Characteristics: Natural resin - translucent, off-white hemispheres. Low melt shrinkage, graphite powder filled. High stability in harsh thermal, chemical and ultraviolet environments. High toug.. |
|||
Tensile Strength, Yield | 34.0 - 50.0 MPa | 4930 - 7250 psi | ASTM D638 |
Arkema Group VOLTALEF® 300 HD PCTFE VOLTALEF® 300 HD is a chlorotrifluoroethylene powder. Used for compression molding, very good flow, non-flammable. Information provided by Arkema Group |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339T20L Talc Reinforced |
|||
Tensile Strength, Yield | 34.0 - 52.0 MPa | 4930 - 7540 psi | ASTM D638 |
Arkema Group KYNAR® 460 Polyvinylidene Fluoride Homopolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Broad molecular weight distribution. High stability in harsh thermal, chemical and ultraviolet environments. High toughness a.. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | |
UBE UBEPOL BR15HB HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %) Description: UBEPOL-BR15HB is characterized by the highest branching of these 3 grades and is adapted by many PS manufacturers.Information provided by UBE. |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | ISO 527 |
Unipetrol PP MONSTEN® GB 218 Polypropylene Homopolymer Applications include injection molding and fibers. Anti Gasfading stabilization. Homopolymer.Information provided by Unipetrol RPA |
|||
Tensile Strength, Yield | 34.0 MPa | 4930 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON MFD03 PP LNP* STAT-KON* MFD03 is a compound based on Polypropylene resin containing 15% Glass Fiber. Added features of this material include: Electrically Conductive. |