SABIC Innovative Plastics LNP LUBRICOMP MX91206 PP

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP MX91206 PP.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* MX91206 is a compound based on Polypropylene containing proprietary fillers. Added feature of this grade is: Wear Resistant.
Physical Properties Metric English Comments
Specific Gravity 0.940 g/cc
0.940 g/cc
ASTM D792
Density 0.940 g/cc
0.0340 lb/in³
ASTM D792
Moisture Absorption 0.0100 %
0.0100 %
50% RH, 24 hrs; ASTM D570
0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow >= 0.020 cm/cm

@Time 86400 sec
>= 0.020 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
0.010 - 0.030 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 15.0 MPa
2180 psi
5 mm/min; ISO 527
21.0 MPa
3050 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 34.0 MPa
4930 psi
5 mm/min; ISO 527
36.0 MPa
5220 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 43.4 %
43.4 %
Type I, 5 mm/min; ASTM D638
55.4 %
55.4 %
5 mm/min; ISO 527
Elongation at Yield 7.8 %
7.8 %
Type I, 5 mm/min; ASTM D638
8.0 %
8.0 %
5 mm/min; ISO 527
Tensile Modulus 1.73 GPa
251 ksi
1 mm/min; ISO 527
2.08 GPa
302 ksi
50 mm/min; ASTM D638
Flexural Strength 40.0 MPa
5800 psi
ISO 178
Flexural Modulus 1.58 GPa
229 ksi
2 mm/min; ISO 178
1.71 GPa
248 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.470 J/cm
0.881 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.83 J/cm
14.7 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 4.00 J

@Temperature 23.0 °C
2.95 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.68
0.68
ASTM D3702 Modified
Coefficient of Friction, Static 0.59
0.59
ASTM D3702 Modified
K (wear) Factor 32.2 x 10-8 mm³/N-M
16.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 84.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
46.7 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 97.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
53.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 99.0 °C
210 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
122 °C

@Thickness 3.20 mm
252 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 63.0 °C
145 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
68.0 °C

@Thickness 3.20 mm
154 °F

@Thickness 0.126 in
unannealed; ASTM D648