- Polymer Property : Tensile Strength, Yield = 12200 psi
Polymer Property : Tensile Strength, Yield = 12200 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 84.0 MPa @Temperature 22.0 °C |
12200 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Menzolit Menzolit® SMC 1500 Unsaturated Polyester UP SMC 1500 is a special SMC for applications calling for high continuous service temperature. The glass level has been selected to combine good mouldability with good strength and stiffness properties.. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Lubricomp KFL36XXC Acetal Copolymer (Europe-Africa-Middle East) LNP* Lubricomp* KFL36 is an Acetal containing Glass Fiber and PTFE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP RN001S PA 66 (Asia Pacific) LNP* Lubricomp* RN001S is a compound based on Nylon 66 resin containing MOS2. Added features of this material include: Internally Lubricated, Heat Stabilized. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP RX01514 PA 66 LNP* LUBRICOMP* RX01514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP RX01514 PA 66 (Asia Pacific) LNP* Lubricomp* RX01514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength, Yield | 84.1 MPa | 12200 psi | ASTM D638 |
| Techmer ES Elastoblend® PA6/6 GF14 IM L 14% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 14% Filler by WeightAdditive: Lubricant and Impact ModifierFeatures: Lubricant and Impact ModifiedUL File Nu.. |
|||
| Tensile Strength, Yield | 84.1 MPa | 12200 psi | ASTM D638 |
| Techmer ES Elastoblend® PA6/6 GF15 IM HS L 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubri.. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Xenoy® 1760 PBT+PC 11% Glass Reinforced PBT+PC alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Xenoy® 1760 PBT+PC 11% Glass Reinforced PBT+PC alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Xenoy® 1760E PBT+PC 11% Glass Reinforced alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors. High flow version of Xenoy 1760 resin. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP DF0029ER PC (Asia Pacific) LNP* Thermocomp* DF0029ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Flame Retardant. |
|||
| Tensile Strength, Yield | 84.3 MPa | 12200 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® HN-3102G PC, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 84.3 MPa | 12200 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® HN-3102G PC, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp OF004AER PPS (Asia Pacific) LNP* Thermocomp* OF004AER is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.This data was supplied by SA.. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific) LNP* Thermocomp* ZF0049 is a compound based on PPE+PS Blend resin containing Flame Retardant. Added features of this material include: Flame Retardant. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics ULTEM 9085 PEI Blend High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution. |
|||
| Tensile Strength, Yield | 84.1 MPa | 12200 psi | ASTM D638 |
| Techmer ES Electrablend® PA6/6 03002 A MB Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement/Unspecified Filler/Reinfor.Additive: Lubricant, Impact Modifier and Heat StabilizerFeatures: Lubricated, Elec.. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP DF0029ER PC LNP* Thermocomp* DF0029ER is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Flame Retardant. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL GFN1410V PPE+PS (Europe-Africa-Middle East) Noryl* GFN1410V resin is a blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 10 % glass reinforcement. The resin is suitable for injection molding. Noryl GFN1410V resin has.. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ASTM D6368 |
| Solvay TECHNYL® A 208KBK-10N-L PA66, DRY Description: Polyamide 66, highly UV-resistance, toughness modified for injection molding.Available in: Asia PacificProduct Applications: TECHNYL A 208K BK 10N-L is used in all sectors of industry, .. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ASTM D638 |
| Cresset Powers Cress-Alon™ A2350 2.35 r.v. Injection Molding Grade Nylon 6, Dry As Molded Neat resin, for injection molding.Information provided by Cresset Powers Ltd. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | DAM; ISO 527-1/-2 |
| DuPont Performance Polymers Zytel® E53 NC010 Nylon 66 Unreinforced High Viscosity Polyamide 66 Information provided by DuPont Performance Polymers |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | 5 mm/min; ISO 527 |
| Eurostar Starflam PX05004 PA66, Glass Fiber Filled, Flame Retardant, Injection Molded Starflam PX05004 is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Eurostar. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | 5 mm/min; ISO 527 |
| Eurostar Starflam PX06010 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded Starflam PX06010 is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | 2 in/min; ASTM Test |
| BASF Ultramid® 8270 HS PA6 (Dry) Ultramid 8270 HS is a thermally modified PA6 blow molding compound exhibiting exceptional toughness and melt strength ideally suited for blow molding, profile extrusion, and other applications requi.. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO R527 |
| Arkema Group Orgalloy® RS 6010 Polyamide 6 Alloy 10% Glass Fiber reinforced Polyamide Alloy, Rigid grade, Nylon 6 basedMolding of Engineering PartsInformation provided by Arkema Group |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | 50mm/min; ISO 527 |
| BASF Ultramid® C3U BK23079 PA66/6 (Dry) Ultramid C3U BK23079 is an injection molding, general purpose PA66/6, pigmented black grade with improved flame retardance. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO 527 type 1 A |
| Solvay TECHNYL® A 303 Natural FA PA66, DRY Description: Unreinforced polyamide PA66, very high viscosity, for extrusion.Available in: Europe Product Applications: TECHNYL® A 303 Natural FA offers three main advantages: high impact resistanc.. |
|||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | DAM; ISO 527-1/-2 |
| DuPont Performance Polymers Zytel® E41HSB NC010 Nylon 66
(Unverified Data**) Unreinforced Heat Stabilized High Viscosity Polyamide 66 Zytel E41HSB is an unreinforced high viscosity heat stabilized polyamide 66 for injection molding and extrusion.Information provided by DuPon.. |
|||
| Tensile Strength, Yield | 84.1 MPa | 12200 psi | ASTM 638 |
| PlastxWorld CEVIAN® B5523 15% GF PBT/ABS Alloy Glass fiber reinforced and flame retarded PBT/ABS alloy.Information provided by PlastxWorld Inc. |
|||