BASF Ultramid® 8270 HS PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8270 HS PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8270 HS is a thermally modified PA6 blow molding compound exhibiting exceptional toughness and melt strength ideally suited for blow molding, profile extrusion, and other applications requiring extra high melt viscosity. It exhibits excellent permeability and chemical resistance to oils, hydrocarbons and most solvents.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 1.6 %
1.6 %
24 hour; ISO Test
9.2 %
9.2 %
ISO 62
Moisture Absorption at Equilibrium 2.6 %
2.6 %
23°C/50% R.H.; ISO 62
Viscosity Measurement 220
220
Formic Acid
Mechanical Properties Metric English Comments
Hardness, Rockwell R 99
99
ASTM Test
Tensile Strength, Yield 84.0 MPa
12200 psi
50mm/min; ISO 527
84.0 MPa
12200 psi
2 in/min; ASTM Test
24.0 MPa

@Temperature 120 °C
3480 psi

@Temperature 248 °F
ISO Data
24.0 MPa

@Temperature 120 °C
3480 psi

@Temperature 248 °F
ASTM Test
138 MPa

@Temperature -40.0 °C
20000 psi

@Temperature -40.0 °F
ASTM Test
138 MPa

@Temperature -40.0 °C
20000 psi

@Temperature -40.0 °F
ISO Data
Elongation at Break >= 100 %
>= 100 %
2 in/min; ASTM Test
Elongation at Yield 4.0 %
4.0 %
50mm/min; ISO 527
4.0 %
4.0 %
2 in/min; ASTM Test
Flexural Strength 114 MPa
16500 psi
ASTM Test
17.0 MPa

@Temperature 120 °C
2470 psi

@Temperature 248 °F
ASTM Test
20.0 MPa

@Temperature 93.0 °C
2900 psi

@Temperature 199 °F
ASTM Test
30.0 MPa

@Temperature 65.0 °C
4350 psi

@Temperature 149 °F
ASTM Test
179 MPa

@Temperature -40.0 °C
26000 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 0.310 GPa
45.0 ksi
2.90 GPa
421 ksi
ASTM Test
0.260 GPa

@Temperature 120 °C
37.7 ksi

@Temperature 248 °F
ASTM Test
0.435 GPa

@Temperature 65.0 °C
63.1 ksi

@Temperature 149 °F
ASTM Test
Izod Impact, Notched 0.530 J/cm

@Temperature -40.0 °C
0.993 ft-lb/in

@Temperature -40.0 °F
ASTM Test
0.530 J/cm

@Thickness 3.17 mm
0.993 ft-lb/in

@Thickness 0.125 in
ASTM Test
Thermal Properties Metric English Comments
CTE, linear 135 µm/m-°C

@Temperature -30.0 - 30.0 °C
75.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 169 °C
336 °F
ASTM Test
Deflection Temperature at 1.8 MPa (264 psi) 63.0 °C
145 °F
ASTM Test
Flammability, UL94 HB
HB
HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Blow Molding
Processing Blow molding
Injection Molding
Special characteristic Heat stabilized or stable to heat
UL.UL-C Yes